Disertación de Maestría
DOI
10.11606/D.88.2005.tde-15122010-094209
Documento
Autor
Nombre completo
Rafael Nucci
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Casteletti, Luiz Carlos (Presidente)
Bolfarini, Claudemiro
Canale, Lauralice de Campos Franceschini
Título en portugués
Avaliação da resistência ao desgaste de cermets depositados pelo processo HVOF e do cromo duro eletrolítico
Palabras clave en portugués
Aspersão térmica
Cromo duro
Desgaste
HVOF
Resumen en portugués
Desgaste é um dos três principais problemas industriais comumente encontrados, que levam à substituição de componentes e equipamentos em engenharia. A possibilidade de se recuperar esses componentes, ou prepará-Ios para suportar melhor as condições de trabalho, é constantemente estudada e novas técnicas são propostas, sempre no sentido de aumentar a vida útil e reduzir custos operacionais. Esta é a razão para o aumento da importância dos sistemas de revestimentos. O cromo duro eletrolftico tem sido muito utilizado para conferir resistência ao desgaste elou à corrosão, porém as características do processo de deposição eletrolítica do mesmo, com a presença do cromo hexavalente, altamente cancerígeno, têm resultado numa limitação crescente ao seu uso. Devido a isso se tomou necessário o desenvolvimento de novos revestimentos alternativos menos agressivos. Os substitutos mais promissores são os "cermets" depositados pelo processo HVOF, que foram produzidos no presente trabalho e comparados com o cromo duro eletrolítico quanto à resistência ao desgaste. Os revestimentos obtidos foram caracterizados por meio de ensaios micrográficos óticos, eletrônicos, raios-x, densidade e ensaios de desgaste dos seguintes tipos: roda de borracha e areia a seco, ensaio abrasivo para carbonetos e micro-abrasivo. O revestimento Cr3 Cr2-NiCr apresentou desempenho geral inferior ao do cromo duro. Entretanto no caso do desgaste micro-abrasivo, onde o mecanismo de desgaste apresentado no mesmo foi misto adesivo-abrasivo, ao contrário dos demais que tiveram características abrasivas, sua resistência ao desgaste foi superior a dos demais. O revestimento constituído de WC-CoCr apresentou o melhor desempenho entre todos os avaliados, o que o indica como um candidato altamente promissor à substituição do cromo
Título en inglés
Evaluation of wear resistance of cermets deposited by HVOF and electroplated hard chrome
Palabras clave en inglés
Hard chrome
HVOF
Thermal spray
Wear
Resumen en inglés
Wear is one of the three main industrial problems, that causes the substitution of components and equipments in engineering. The possibility to recover those components or to prepare them to better support the work conditions is constantly studied and new techniques are proposed, a/ways seeking to increase the life span and to reduce operational eosts. This is the reason why the coating systems are important. The hard ehrome coatings has been traditionally used to improve wear resistance and/or eorrosion resistance. However the eharacteristics of the electroplated deposition proeess, with the presence of the hexavalente ehrome, highly cancerous, result in a growing limitation to its use. Due to that it beeome necessary the development of new less aggressive alternative eoatings. The most promising substitutes are the "cermets" deposited by the HVOF process that were produced in the present work and compared with electroplated hard ehrome coatings for wear resistance. The obtained coatings were characterized through optical and electronic mierographics analysis , x-ray, density and submitted to the following types of wear tests: Dry Sand I rubber wheel, Wear test for cemented carbides and mieroabrasive wear test. The coating Cr3Cr2-NiCr presented smaller general performance in comparison with the hard ehrome. However, in the case of the miero-abrasive wear, where the wear mechanism presented was mixed adhesive-abrasive, unlike the others that had only abrasive eharacteristics, the resistance to the wear was superior. The WC-CoCr coating presented the best performance overall, what indicates it as a candidate to the hard ehrome substitution
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
RafaelNucciM.pdf (16.36 Mbytes)
Fecha de Publicación
2010-12-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.