Tesis Doctoral
DOI
10.11606/T.88.2005.tde-15122010-095113
Documento
Autor
Nombre completo
Alessandra Etuko Feuzicana de Souza Almeida
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Sichieri, Eduvaldo Paulo (Presidente)
Baldo, João Baptista
Boschi, Anselmo Ortega
Ferreira, Osny Pellegrino
Sabbatini, Fernando Henrique
Título en portugués
Estudo da influência das adições de sílica ativa e copolímero estireno acrílico nas propriedades de argamassas para assentamento de porcelanato
Palabras clave en portugués
Argamassa colante
Microestrutura
Polímero
Porcelanato
Sílica ativa
Resumen en portugués
Apesar de suas excelentes características técnicas e estéticas, a aplicação de porcelanato em fachadas requer especial atenção devido ser um material diferente das cerâmicas convencionais, além de que as fachadas estão sujeitas a diversos agentes capazes de danificar os revestimentos cerâmicos. O baixo índice de absorção de água do porcelanato é a principal causa da perda ou falta de aderência entre o tardoz e a argamassa colante, pois não permite o mecanismo de aderência mecânica existente nas cerâmicas porosas. O presente trabalho visa o estudo de argamassas com adições de látex base estireno acrílico e sílica ativa para o assentamento de porcelanato em fachadas a fim de evitar o aparecimento de patologias decorrentes da falta de aderência. Foram realizados ensaios normalizados para a avaliação das propriedades das argamassas quanto à fixação do porcelanato, além de procedimentos experimentais para a avaliação da microestrutura tais como análises térmicas, difração de raios-X, porosimetria por intrusão de mercúrio, espectroscopia de infravermelho e microscopia eletrônica de varredura associada à espectrografia por dispersão de energia. Os resultados obtidos mostraram que a adição combinada de polímero e sílica ativa às argamassas resultou em elevadas propriedades mecânicas e alta resistência de aderência, decorrentes da melhora das propriedades microestruturais, ou seja, aumento da compacidade, diminuição da porosidade e refinamento do diâmetro médio dos poros, além da redução na quantidade do hidróxido de cálcio consumido para a produção de silicato de cálcio hidratado.
Título en inglés
Study of the copolymer styrene acrylic and silica fume adittions influence in the properties of mortars to fix porcelain stoneware tiles
Palabras clave en inglés
Adhesive mortar
Microestruture
Polymer
Porcelain tile
Silica fume
Resumen en inglés
Despite the excellent characteristics of porcelain tiles, their application in building facades requires special attention, since this material differs from conventional ceramics and facades are exposed to weathering, which can damage ceramic revetments. The lower water absorption of porcelain tiles is the main cause of the poor adherence between them, as it prevents the mechanical interlocking adherence mechanism that occurs when more porous ceramic materials are applied. The present thesis aims to investigate the effect of silica fume and acrylic polymer together on the properties of mortars employed to install porcelain stoneware tiles to avoid detachment problems due to lack of adherence. An experimental investigation evaluated the fixing properties of the mortars, and a microstructural study including thermal analysis, X-ray diffraction, mercury intrusion porosimetry, infrared spectroscopy and scanning electron microscopy was performed. The results showed that silica fume and acrylic polymer addition to the mortar resulted in improved properties to fix porcelain stoneware tiles, mainly adherence strength, as a consequence of the microstructural improvement due to the decrease in the porosity and the pore mean diameter, and the decrease in the calcium hydroxide to form hydrated calcium silicate
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-12-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.