Thèse de Doctorat
DOI
10.11606/T.88.2005.tde-15122010-095113
Document
Auteur
Nom complet
Alessandra Etuko Feuzicana de Souza Almeida
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2005
Directeur
Jury
Sichieri, Eduvaldo Paulo (Président)
Baldo, João Baptista
Boschi, Anselmo Ortega
Ferreira, Osny Pellegrino
Sabbatini, Fernando Henrique
Titre en portugais
Estudo da influência das adições de sílica ativa e copolímero estireno acrílico nas propriedades de argamassas para assentamento de porcelanato
Mots-clés en portugais
Argamassa colante
Microestrutura
Polímero
Porcelanato
Sílica ativa
Resumé en portugais
Apesar de suas excelentes características técnicas e estéticas, a aplicação de porcelanato em fachadas requer especial atenção devido ser um material diferente das cerâmicas convencionais, além de que as fachadas estão sujeitas a diversos agentes capazes de danificar os revestimentos cerâmicos. O baixo índice de absorção de água do porcelanato é a principal causa da perda ou falta de aderência entre o tardoz e a argamassa colante, pois não permite o mecanismo de aderência mecânica existente nas cerâmicas porosas. O presente trabalho visa o estudo de argamassas com adições de látex base estireno acrílico e sílica ativa para o assentamento de porcelanato em fachadas a fim de evitar o aparecimento de patologias decorrentes da falta de aderência. Foram realizados ensaios normalizados para a avaliação das propriedades das argamassas quanto à fixação do porcelanato, além de procedimentos experimentais para a avaliação da microestrutura tais como análises térmicas, difração de raios-X, porosimetria por intrusão de mercúrio, espectroscopia de infravermelho e microscopia eletrônica de varredura associada à espectrografia por dispersão de energia. Os resultados obtidos mostraram que a adição combinada de polímero e sílica ativa às argamassas resultou em elevadas propriedades mecânicas e alta resistência de aderência, decorrentes da melhora das propriedades microestruturais, ou seja, aumento da compacidade, diminuição da porosidade e refinamento do diâmetro médio dos poros, além da redução na quantidade do hidróxido de cálcio consumido para a produção de silicato de cálcio hidratado.
Titre en anglais
Study of the copolymer styrene acrylic and silica fume adittions influence in the properties of mortars to fix porcelain stoneware tiles
Mots-clés en anglais
Adhesive mortar
Microestruture
Polymer
Porcelain tile
Silica fume
Resumé en anglais
Despite the excellent characteristics of porcelain tiles, their application in building facades requires special attention, since this material differs from conventional ceramics and facades are exposed to weathering, which can damage ceramic revetments. The lower water absorption of porcelain tiles is the main cause of the poor adherence between them, as it prevents the mechanical interlocking adherence mechanism that occurs when more porous ceramic materials are applied. The present thesis aims to investigate the effect of silica fume and acrylic polymer together on the properties of mortars employed to install porcelain stoneware tiles to avoid detachment problems due to lack of adherence. An experimental investigation evaluated the fixing properties of the mortars, and a microstructural study including thermal analysis, X-ray diffraction, mercury intrusion porosimetry, infrared spectroscopy and scanning electron microscopy was performed. The results showed that silica fume and acrylic polymer addition to the mortar resulted in improved properties to fix porcelain stoneware tiles, mainly adherence strength, as a consequence of the microstructural improvement due to the decrease in the porosity and the pore mean diameter, and the decrease in the calcium hydroxide to form hydrated calcium silicate
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2010-12-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.