Master's Dissertation
DOI
10.11606/D.88.2011.tde-16082011-154048
Document
Author
Full name
Marcos Miranda
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2011
Supervisor
Committee
Tarpani, José Ricardo (President)
Carvalho, Jonas de
Silva, Valdinei Ferreira da
Title in Portuguese
Comparação entre métodos de inspeção não-destrutiva aplicados a peças compósitas laminadas sólidas estruturais aeronáuticas
Keywords in Portuguese
Danos e defeitos de manufatura
Ensaios não destrutivos
Laminados compósitos poliméricos
Abstract in Portuguese
Diversos métodos de ensaios não-destrutivos (Ultrasom, Radiografia, Termografia e Shearografia) foram empregados na inspeção de peças laminadas estruturais compósitas sólidas de matriz polimérica manufaturadas pela indústria aeronáutica. Concluiu-se que Ultrasom pulso-eco convencional de contato foi a técnica mais abrangente na indicação de descontinuidades (danos/defeitos de manufatura) considerando-se peças planas e curvas, não obstante tenha falhado na detecção de trincas longas e bem definidas localizada na alma de componentes co-curados. Radiografia convencional por filmes exibiu um potencial interessante como método alternativo, ou complementar ao de Ultrasom. Termografia infravermelha foi a técnica mais veloz na indicação de descontinuidades, sendo uma valiosa alternativa para um mapeamento rápido em inspeções preliminares seguidas pela aplicação de técnicas complementares. Shearografia realizada com equipamento da empresa Photonita detectou inclusões em peça plana compósita, porém a interpretação dos resultados obtidos em geometrias mais complexas se mostrou duvidosa. O uso de equipamento shearográfico da empresa Dantec indicou posições em regiões curvas que podem estar associadas à presença de defeitos/danos locais, porém uma confirmação cabal desta relação não foi efetivada. Evidências visuais da profusa presença de danos/defeitos de manufatura, além da existência de detalhes construtivos nas peças compósitas mais complexas, sugerem que estas descontinuidades podem ter sensibilizado, em maior ou menor extensão, os equipamentos END, juntamente com a eventual presença de delaminações/falhas de adesão nas respectivas peças avaliadas.
Title in English
Comparing nondestructive inspection methods applied to aeronautical grade solid structural composite laminated parts
Keywords in English
Manufacturing damages and defects
Nondestructive inspection
Polymer composite laminates
Abstract in English
Several nondestructive methods (Ultrasonics, Radiography, Thermography and Shearography) were employed for inspection of structural polymer matrix composite laminated parts manufactured by aircraft industry. Is has been concluded that conventional pulse-echo contact Ultrasonics was the most comprehensive technique to indicate discontinuities (manufacture damages/defects) in flat and curved parts, although it has failed to detect long and well-defined cracks in co-cured components. Conventional film radiography exhibited good potential as alternative or complementary method to Ultrasonics. Infrared thermography was the fastest technique to indicate discontinuities, so that it is a valuable option for rapid mapping in preliminary inspection followed by the application of complementary techniques. Sherography by means of Photonita equipment detected inclusions in flat panels, but the interpretation of results from pieces with more complex geometries was dubious. A shearographic of the Dantec device indicated positions in curved regions which might possibly be associated to the presence of damages/defects, however this relationship could not be definitively established. Visual evidences of the profuse existence of manufacture damages/defects, besides constructive details in more complex composite parts, suggest that theses discontinuities might have affected to some extent the NDT equipments, along with the eventual presence of delaminations/lack of adhesion on the respective evaluated parts.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2012-01-16
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.