Doctoral Thesis
DOI
10.11606/T.88.2016.tde-16092016-160549
Document
Author
Full name
Adnauêr Tarquinio Daltro
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2000
Supervisor
Committee
Gomes, Samuel Irati Novaes (President)
Bolfarini, Claudemiro
Calil Júnior, Carlito
Ferraresi, Valtair Antonio
Malite, Maximiliano
Title in Portuguese
Soldagem a arco elétrico com proteção gasosa em juntas de chapas finas de aço
Keywords in Portuguese
Aço zincado
Chapa fina
Distorções
Soldagem
Abstract in Portuguese
O uso de chapas finas de aço, revestidas ou não, tem sido crescente nos últimos anos, principalmente aquelas que tem revestimento à base de zinco. Isto ocorre tanto na indústria automobilística e mecânica como na construção civil, que geralmente fabricam suas peças e estruturas utilizando um procedimento de soldagem. O objetivo deste trabalho é estabelecer procedimentos de soldagem à arco elétrico com proteção gasosa - GMAW - com transferência por curto circuito, para elementos de chapa fina de aço carbono não revestido e aço zincado, de modo a se obter junções de qualidade aceitável e diminuição das distorções decorrentes dos ciclos térmicos presentes durante a soldagem e, consequentemente a redução das tensões residuais. Em termos de qualidade da solda, propões-se uma combinação de consumíveis disponíveis no mercado, de modo a reduzir os defeitos como: porosidade, respingos, trincas e perda de revestimento. No caso das chapas finas de aço zincado, a melhor combinação de consumíveis encontrada foi: arame com baixo teor de desoxidantes, ER70S-3, e como gás de proteção a mistura 8% CO2 + 92% Ar. Quanto à redução e controle das distorções, três técnicas são utilizadas. A técnica que utiliza em escoadouro dinâmico de calor, formado por um jato de gás refrigerador aplicado logo após o arco de solda durante a soldagem, apresentou maior eficiência na redução das distorções, provenientes do ciclo térmico.
Title in English
Gas metal arc welding of thin sheet steels
Keywords in English
Distortion
Galvanized steel
Thin sheet
Welding
Abstract in English
The thin sheet steels, coated or not, has been widely used nowadays, mainly the hot dip galvanized steel sheets. It's observed as in the mechanic and automobilist industry as in the civil construction that in manufacturing of pieces and structures employ welding procedures. The aim of this work is to establish procedures to gas metal are welding with short circuit transfer of thin sheet steel elements, not coated and zinc-coated steel, in order to get junctions of acceptance quality and reduction of welding stress and distortion. This distortion arise of the thermal cycles that occur during the welding. In terms of the weld quality is defined the best consumables combination available in the market, in such a way to reduce the weld defects like porosities, spatters, cracks and loss of covering. To galvanized steel sheets, the combination: wire ER70S-3 and mixture 8%CO2 + 92% Ar showed the best performance. Three techniques were employed for control and reduce the welding distortion. One that using a spot heat sink following the arc, in this case the cooling jet, was more efficient that others techniques.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2016-09-19
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.