Master's Dissertation
DOI
10.11606/D.88.1998.tde-19042002-142153
Document
Author
Full name
Rosana Vilarim da Silva
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1998
Supervisor
Committee
Bose Filho, Waldek Wladimir (President)
Ferreira, Itamar
Spinelli, Dirceu
Title in Portuguese
Avaliação da tenacidade à fratura de soldas de alta resistência e baixa liga pelo método da integral-J.
Keywords in Portuguese
integral-J
soldas ARBL
tenacidade à fratura
variação da flexibilidade elástica
Abstract in Portuguese
Foi avaliada a influência da microestrutura na tenacidade à fratura de dois grupos de aços de Alta Resistência e Baixa Liga (ARBL), soldados, com diferentes composições microestruturais. Os metais de solda designados por A1/A2 exibiram uma microestrutura composta por ferrita acicular circundada por ferrita de contorno de grão, com alguma formação de ferrita Widmanstätten e microfases, denominada de microestrutura do tipo clássica. Os metais de solda designados por B1/B2 exibiram um microestrutura composta por bainita, martensita de baixo teor de carbono e microfases, denominada de microestrutura do tipo de ripas. Estes dois tipos de microestruturas são normalmente encontradas nas soldas de alta resistência empregadas em estruturas e componentes de grande responsabilidade. A avaliação da tenacidade à fratura foi realizada pela utilização dos conceitos da integral-J e CTOD. A técnica empregada para a medida do crescimento da trinca, foi a da variação da flexibilidade elástica em corpos de prova SE[B] e C(T). Os valores da tenacidade à fratura dos dois grupos de soldas, para ambas geometrias de corpos de prova, foram determinados e comparados. As análises microestruturais, do metal de solda e das superfícies de fratura dos corpos de prova ensaiados, foram realizadas por meio de microscopia ótica e eletrônica de varredura, com o objetivo de se correlacionar os valores de tenacidade à fratura com a microestrutura dos metais de solda. Foi verificado que os metais de solda A1/A2 que possuem uma microestrutura clássica, apresentaram tenacidade superior aos metais de solda B1/B2, que possuem uma microestrutura do tipo de ripas.
Title in English
Evaluation of high strength low alloy steel weld metal fracture toughness using the J-integral method.
Keywords in English
elastic compliance technique
fracture toughness
HSLA weld metals
J-integral
Abstract in English
The influence of the microstructure on the fracture toughness behaviour of two groups of multipass High Strength Low Alloy (HSLA) steel weld metals, presenting different microstructure composition, was evaluated. The weld metals A1/A2 exhibited a microstructure composed by acicular ferrite, allotriomorphic ferrite, Widmanstätten ferrite and microphases, and the weld metals B1/B2 presented a microstructure composed by bainite, low carbon martensite and microphases. The fracture toughness evaluation was carried out using J-integral and CTOD concepts and the elastic compliance technique in both SE[B] and CT testpieces. The fracture toughness values for both groups of welds and testpiece geometry were determined and compared. The weld metals microstructures and fracture surfaces analysis were performed using optical and scanning electronic microscope techniques, to correlate the determined fracture toughness values, with the local microstructure around the fatigue crack tip. It was verified that the weld metals A1/A2 exhibited fracture toughness values superior to the ones obtained from weld metals B1/B2.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
disrosanavilarin.pdf (5.72 Mbytes)
Publishing Date
2002-12-20
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.