Disertación de Maestría
DOI
10.11606/D.88.2013.tde-19042013-205354
Documento
Autor
Nombre completo
Rita de Cássia Costa Dias
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Tarpani, José Ricardo (Presidente)
Botelho, Edson Cocchieri
Riva, Rudimar
Título en portugués
Microescultura por laser de superfícies metálicas para manufatura de laminados híbridos metal/fibra
Palabras clave en portugués
Adesão metal-polímero
Laminado híbrido metal-fibra
Laser em manufatura
Resumen en portugués
Este trabalho objetivou a manufatura de laminados híbridos metal-fibra (LMF) empregando-se chapas com 0,5 mm de espessura de liga-'TI'6'AL'4'V' com superfícies modificadas por laser de fibra de modo a otimizar a sua adesão com polímero termoplástico poli-sulfeto de fenileno (PPS). Observou-se que a microtextura superficial da liga metálica dependeu fortemente da potência do feixe laser, quando potências mais baixas levaram à verdadeira texturização da superfície metálica, enquanto que potências mais elevadas conduziram à ablação da mesma. A texturização superficial metálica sob laser de baixa potência aparentou ser a condição mais apropriada para a adesão metal-polímero por ancoragem mecânica de macromoléculas, o que foi contrabalanceado por elevados níveis de tensão residual das chapas metálicas, gerando grande distorção das mesmas e inviabilizando sua utilização. O emprego de uma potência intermediária (160 W) mostrou-se propício à otimização entre a adesão física entre metal-polímero e o nível de tensões residuais criado nas chapas metálicas. Concluiu-se que os espécimes extraídos do centro dos laminados metal-fibra exibem uma tensão limite média para falha por cisalhamento interlaminar consideravelmente superior à dos espécimes usinados a partir da borda dos LMF. O LMF manufaturado sob maiores pressão e temperatura exibiu uma maior compactação e melhor consolidação, culminando num máximo desempenho médio sob carga de cisalhamento interlaminar. Evidências de uma correlação entre o mecanismo de falha por cisalhamento interlaminar do corpo de prova e o seu nível de resistência a este tipo de carregamento mecânico foram documentadas e discutidas.
Título en inglés
Laser microesculpture of metallic surfaces to hybrid fiber-metal laminates
Palabras clave en inglés
Hybrid fiber-metal laminate
Laser in manufacturing
Metal-polymer adhesion
Resumen en inglés
This work aimed at manufacturing hybrid fiber-metal laminates (FML) by employing 0,5 mm-thick 'TI'6'AL'4'V'-alloy plaques with fiber laser modified surface in order to optimize metal adhesion with poli-phenylene sulfide (PPS) thermoplastic polymer. The surface microtexture of metallic alloy strongly depended upon the laser power, inasmuch as low-power laser led to true texturization of metal surface, whereas high-power laser light drove to its ablation. Surface metal texturization under low-power laser apparently was the most appropriate condition to metal-polymer adhesion via mechanical entanglement of macromolecules, which was offset by high levels of residual stresses on metallic plaques, bringing them quite warped and useless. The use of an intermediate laser power (160 W) has been shown benign to the optimization between metal-polymer physical adhesion and the residual stress level created in the metal plates. It has been concluded that testpieces machined from the FML central position exhibited average ultimate interlaminar shear strenght considerably higher than those extracted from the FML borders. The FML manufactured under higher pressure and temperature was more compacted and better consolidated, so that it displayed the greatest average performance under interlaminar shear loading. Evidences of a correlation between the failure mechanism by interlaminar shearing of test coupon and its allowance to this type of mechanical loading were documented and discussed.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
RitaMECorrigida.pdf (4.95 Mbytes)
Fecha de Publicación
2013-04-25
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.