Disertación de Maestría
DOI
10.11606/D.88.2000.tde-20012011-101938
Documento
Autor
Nombre completo
Mauricio Carvalho da Cunha
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Gregolin, José Ângelo Rodrigues
Ierardi, Maria Clara Filippini
Título en portugués
Influência de parâmetros de processo no crescimento de trincas curtas por fadiga em camada cementada do aço DIN 20MnCr5.
Palabras clave en portugués
Cementação
Jateamento por granalhas
Oxidação intergranular
Propagação de trincas curtas por fadiga
Revenimento
Resumen en portugués
Os tratamentos de cementação, têmpera, revenimento e jateamento por granalhas são muito utilizados na produção seriada de peças da indústria automobilística, como engrenagens e eixos. Variações destes processos podem influenciar a vida em fadiga por flexão dos componentes descritos. O objetivo deste trabalho foi estudar a influência de variações no tempo de jateamento por granalhas, variações na temperatura de revenimento e de diferentes profundidades de oxidação intergranular, no crescimento de trincas curtas por fadiga na camada cementada do aço DIN 20MnCr5. Para isso foram feitos ensaios de fadiga por flexão em quatro pontos, utilizando corpos de prova de seção retangular e sem entalhe. Para o acompanhamento do crescimento de trincas curtas foi utilizado o método de réplicas de acetato. Foram estudados seis níveis de jateamento, quatro níveis de revenimento e dois níveis de oxidação intergranular. Como resultados principais, foram obtidas curvas de comprimento de trinca por número de ciclos e taxa de crescimento de trinca por tamanho médio da trinca. Amostras jateadas entre trinta minutos e uma hora, revenidas à 160°C e com oxidação intergranular por volta de dez mícrons, apresentaram os melhores resultados em relação à vida em fadiga.
Título en inglés
The influence of manufacturing process parameters on short fatigue crack growth in a carburized case.
Palabras clave en inglés
Carburizing
Internal oxidation
Short fatigue crack propagation
Shot peening
Tempering
Resumen en inglés
Carburizing, quenching, tempering and shot peening treatments are often used in mass production of automotive parts, such as gears and shafts. Changes in these treatments can influence the bending fatigue life of these parts. The purpose of this study was to measure the influence of different shot peening times, different tempering temperature and different internal oxidation depths, on the short fatigue crack growth in case carburized DIN 20MnCr5 steel. Four-point-bend fatigue tests were carried out in rectangular section specimens without notch. The surface short crack growth was monitored by means of acetate replication technique. Six levels of shot peening, four levels of tempering temperatures and two levels of internal oxidation were studied in this work. Crack length versus number of cycles and crack growth rate versus mean crack length were obtained as principal results. Shot peening from 30 minutes to one hour, tempering at 160#176C and a lO~m depth of internal oxidation showed the best results in fatigue life.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-01-31
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.