Disertación de Maestría
DOI
10.11606/D.88.2002.tde-20082015-165222
Documento
Autor
Nombre completo
Mario Godinho Junior
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2002
Director
Tribunal
Leite, Edson Roberto (Presidente)
Andreeta, Marcello Rubens Barsi
Lanfredi, Silvania
Título en portugués
Síntese e caracterização do BIMEVOX pelo método dos precursores poliméricos
Palabras clave en portugués
BIMEVOX
Condutor iônico
Eletrólito sólido
Precursores poliméricos
Resumen en portugués
As cerâmicas do tipo BIMEVOX, onde ME= metal dopante com estequiometria Bi4Me2xV2(1-x)Ox(11-3x), são conhecidas como eletrólitos sólidos e a utilização destes materiais está voltada principalmente para dispositivos como: sensores de oxigênio, células de combustíveis, conversão de energia, baterias e dispositivos associados à condução iônica. Dada a dificuldade de obter-se materiais policristalinos de alta densidade, buscou-se o método dos precursores poliméricos para obter-se um pó com maior área superficial específica e, consequentemente aumentar a densificação, para melhorar assim a condutividade iônica do oxigênio. As cerâmicas BIMEVOX dopadas com 20% de Titânio em relação ao Vanádio (BITIVOX.20) foram as que apresentaram a maior condutividade, sendo de 5,39 x10-4 (Ω.cm)-1 à temperatura de 200 °C com uma a densidade relativa de 98% Esses resultados são uns dos melhores até o momento reportado na literatura
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
The BIMEVOX type ceramics present the general formula Bi4Me2xV2(1-x)Ox(11-3x), in which Me stands for the doping metal. They are known as soiid electrolytes and the utilization of these materiais is mairly directed towards devices such as: oxygen sensors, fuel cells, energy conversion, batteries and devices associated to the ionic conduction. Due to the difficulty of obtaining high density polycrystalline materiais, it was used the polymeric precursor method to produced a powder with higher specific surface area and therefore increase the densification, in order to improve the ionic conductivity of oxygen. BIMEVOX ceramics with titanium presenting a doping levei of 20 mol%, in relation to vanadium, (BITIVOX.20) where the ones that presented the highest conductivity, reaching the value of 5,39 x10-4 (Ω.cm)-1 at the temperature of 200 °C with a relative density of 98%. These figures represent one of the best results reported up to now in the literature
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-08-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.