Doctoral Thesis
DOI
10.11606/T.88.2016.tde-20092016-113125
Document
Author
Full name
Marcia Fernanda Martins Dias
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2002
Supervisor
Committee
Gomes, Samuel Irati Novaes (President)
Canale, Lauralice de Campos Franceschini
Crnkovic, Ovídio Richard
Gregolin, José Ângelo Rodrigues
Mello, José Daniel Biasoli de
Title in Portuguese
Avaliação dos parâmetros de soldagem na resistência ao desgaste abrasivo de revestimentos duros
Keywords in Portuguese
Arco submerso
Desgaste abrasivo
Revestimento duro
Abstract in Portuguese
Este trabalho apresenta uma análise das condições de soldagem sobre o desgaste abrasivo de um revestimento duro. O revestimento foi feito pela deposição metálica por arco submerso variando os parâmetros de soldagem e utilizando fluxos comerciais. Foram utilizados dois conjuntos de parâmetros de soldagem (conjunto 01 com velocidade de soldagem de 55 cm/min, extensão do eletrodo de 35,0 mm, tensão de 30V, corrente de 450A e o conjunto 02 com velocidade de soldagem de 50 cm/min, extensão do eletrodo de 25,5 mm, tensão do arco de 26V e corrente de 440A) e quatro fluxos comerciais (identificados como E, M, L e R) formando assim oito condições de soldagem. Foram feitas duas camadas com três cordões de solda cada sobre uma chapa base de aço SAE 1020. Corrente contínua com polaridade direta (CC-) foi utilizada em ambas condições. A resistência ao desgaste abrasivo a baixa-tensão foi avaliada pelo ensaio de desgaste do tipo Roda de borracha/areia seca conforme a norma ASTM G65-94. A análise microestrutural foi feita por microscopia óptica e a análise da região desgastada por microscopia eletrônica de varredura. A resistência ao desgaste abrasivo dos revestimentos do conjunto 01 foi superior em comparação com os revestimentos do conjunto 02, para todos os fluxos utilizados. Os fluxos E e R proporcionaram os melhores desempenho e a martensita de agulhas foi a microestrutura com a qual foram obtidos os melhores resultados de desgaste abrasivo a baixa-tensão neste estudo realizado.
Title in English
Evaluation of the welding variables on the abrasion resistance of hardfacings
Keywords in English
Abrasive wear
Hardfacing
Submerged arc welding
Abstract in English
This work presents an analysis of the welding conditions and its effects in the abrasive wear of hardfacings. The hardfacings were obtained by submerged arc surfacing. The welding variables were changed and the commercials fluxes were used. Two groups of welding variables were used (group 01: a traveI speed of 55 cm/min, an electrode extension of 35,0 mm, a voltage of 30V and an amperage of 450A; group 02: a traveI speed of 50 cm/min, an electrode extension of 25,0 mm, a voltage of 26V and an amperage of 440A) and four commercials fluxes (E, M, L e R designated) establishing eight welding conditions. Double-Iayered ot three beads were deposited (applied) on a SAE 1020 base metal plate. Direct current electrode negative polarity (CC-) were used in both groups of welding. The low stress abrasion resistance evaluation was carried out by dry sand/rubber wheel apparatus according to the ASTM G65-94. The microstructural analysis were done by optical microscopy and the worn surface analysis were done by scanning electronic microscopy. The abrasion resistance of the group 01 was superior as compared to the group 02, independent of the fluxe was used. The fluxes E and R presented the best results and the befter abrasion resistant microstructure was lath martensite.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Tese_Dias_MarciaFM.pdf (13.31 Mbytes)
Publishing Date
2016-09-20
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.