Tesis Doctoral
DOI
10.11606/T.88.2005.tde-20102005-085923
Documento
Autor
Nombre completo
Carlos Eduardo Marmorato Gomes
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Ferreira, Osny Pellegrino (Presidente)
Baldo, João Baptista
Bretas, Rosário Elida Suman
Souza, Milton Ferreira de
Tarpani, José Ricardo
Título en portugués
"Propriedades da pasta de cimento portland com adições do copolímero Va/VeoVa e fibras de poliamida - estudo da interface fibra-matriz"
Palabras clave en portugués
cimento
copolímero
interface
poliamida
Va/VeoVa
Resumen en portugués
O crescente emprego de compósitos fibrosos pela indústria da construção civil, nos últimos anos, comprova a eficiência da adoção de fibras como reforço de matrizes frágeis, a exemplo das pastas, argamassas e concreto de cimento Portland. Com o desenvolvimento de novas fibras sintéticas em suas propriedades, com custo similar ao das fibras comuns, faz-se supor que os produtos reforçados por essas fibras tenham grande avanço nos próximos anos. Especificamente em relação à fibra poliamida 6.6, constata-se que a mesma possui módulo de elasticidade menor em relação às matrizes de cimento Portland convencionais e pobre interface fibra/matriz. O incremento do módulo de elasticidade dessas fibras constitui grande desafio à industria têxtil devido às características de seu processo de fabricação, especificamente no que se refere à fiação, porém, isso não bastaria, havendo também a necessidade de aumentar sua aderência com as matrizes cimenticias. Dessa maneira, o presente trabalho buscou, pela adição de um copolímero redispersável (Va/VeoVa – vinil acetato/ vinil éster do ácido versático), tornar compatível o valor do módulo de elasticidade da matriz cimentícia ao das fibras de poliamida, além de proporcionar o desenvolvimento da zona de transição interfacial (ZTI), com melhor transferência de tensões entre a matriz de cimento modificada e as fibras de poliamida. Além desses objetivos, o emprego conjunto das tecnologias do cimento/concreto modificado com polímero (CMP) e do cimento/concreto reforçado com fibras (CRF) permitiu à presente pesquisa a exploração de sinergismos em xi propriedades como tenacidade, flexibilidade, resistência à tração e resistência ao impacto. Para caracterização desses compostos, foram realizados ensaios no estado fresco (mini-slump e tempo de pega), ensaios mecânicos (compressão axial, tração na flexão e impacto) e análises microscópicas, com intuito de analisar a interface fibra-matriz e a possível interação química entre o copolímero e a pasta de cimento Portland, por meio das técnicas de Termogravimetria (TG), Difratometria de Raios-X (DRX), Infravermelho por Transformada de Fourier (FT-IR), Porosimetria por Intrusão de Mercúrio (PIM), Microscopia Eletrônica de Varredura (MEV) com sistema de Espectroscopia por Dispersão de Energias (EDS) em amostras fraturadas e Microscopia Eletrônica de Varredura (MEV) por imagem de elétrons retroespalhados (BSEI) em amostras polidas.
Título en inglés
properties of va/veova copolymer modified cement pastes reinforced by polyamide fibers - study of interface fiber-matrix
Palabras clave en inglés
cement
interface
polyamide fiber
Va/VeoVa copolymer
Resumen en inglés
In the last years, the increasing employment of fiber reinforced composites by the building industry shows the efficiency of the fibers as reinforcement of brittle matrices such as the pastes, mortars and Portland cement concrete. The development of the synthetic fibers characteristics with costs that are compatible with other fibers allows us to preview the biggest improvement of the products reinforced by these fibers. In relation to polyamide 6.6 specifically, it is verified that its elasticity modulus is slower compared with the value of conventional Portland cement matrices and poor interface fiber/matrix. The increase of elasticity modulus of these fibers is the biggest challenge for the textile industry due to characteristics of their fabrication, specifically to cord production. But it is not sufficient, because the adherence between polyamide fiber and Portland cement matrices needs to be improved. In this way, the goals of this present research were to make the elasticity modulus of the Portland cement matrix compatible with the elasticity modulus of polyamide fibers and to allow the development of the interfacial transition zone (ITZ) by the addition of the redispersible copolymer Va/VeoVa (acetate-versatate). Moreover, the use of both technologies, fiber reinforcement and polymermodified cement, allowed the present work to reach synergism in several properties, such as toughness, flexibility, traction strength and impact strength. The composites characterization was realized by tests in the fresh state, mechanical tests and microscopic analyses (Thermogravimetric Analyses, X-Ray Diffraction, Fourier-Transform Infrared, Mercury Intrusion Porosity and Scanning Electronic xiii Microscopy), which also had, as goals, to verify possible chemical interaction between copolymer and Portland cement paste.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TeseCemgomes.pdf (48.92 Mbytes)
Fecha de Publicación
2006-02-06
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.