• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.88.1999.tde-22082015-105319
Documento
Autor
Nombre completo
Roberto Messias Bezerra
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Guastaldi, Antonio Carlos (Presidente)
Bose Filho, Waldek Wladimir
Zavaglia, Cecília Amélia de Carvalho
Título en portugués
Estudo de solda a laser em ligas odontológicas utilizadas em prótese sobre implante: titânio comercialmente puro e liga de ouro
Palabras clave en portugués
Liga de ouro
Soldagem a laser
Titânio
Resumen en portugués
Este trabalho consiste no estudo de juntas soldadas de ligas metálicas Odontológicas, Titânio comercialmente puro e liga de ouro, aplicada em próteses sobre implantes, empregando processo de soldagem a laser. A caracterização destes biomateriais e das juntas soldadas foram feitas por meio de técnicas de análise química, análise metalográfica utilizando-se microscopia óptica e microscopia eletrônica de varredura - MEV, com espectroscopia por espalhamento de energia dispersiva de raios X-EDX , espedroscopia por comprimento de onda de raios X - WDX, mapeamento elementar, / difratometria de raios X. Foi estudado também a dureza, correlacionando-as com a microestrutura e composição química. Realizou-se ensaios caracterizando o processo de corrosão nos metais base e nas juntas soldadas, em solução de NaCI 0,15 mol L , utilizando técnica eletroquímica; curva de polarização potenciodinâmica. Na região do cordão de solda, a microestrutura do titânio comercialmente puro foi do tipo martensítica, e na liga ouro paládio, apresentou uma morfologia dendrítica. No titânio, a dureza no metal base foi de 199 HV, menor do que a dureza no cordão de solda, que foi de 421 HV, devido a presença da microestrutura martensítica. Na liga de ouro a dureza no metal base foi de196 HV, maior do que a dureza no cordão de solda, que foi de 103 HV, devido à microestrutura dendrita. Na caracterização da resistência à corrosão os resultados obtidos demonstraram uma menor resistência à corrosão no cordão de solda para ambos os biometeriais no meio estudado
Título en inglés
Not available
Palabras clave en inglés
Not available
Resumen en inglés
This work comprises the study of odontological metallic welded joints, commercially pure titanium and gold alloys, applied to prothesis on implants, employing laser welding process. The characterization of these biomaterials and welded joints was made by means of chemical and metallographic analysis, by using optical and scanning electron microscopy (SEM) technique with Energy Dispersive X Rays analysis (EDX), elemental mapping, and X-Ray Difractometry. Experimental tests were carried out characterizing the corrosion process in metal base and welded joints, in NaCI solution 0.15 mo L-1, using electrochemical techniques, potentiodynamic polarization curve. The correlation among hardness, microstructure and chemical composition was aiso studied. In the welding region, the commercially pure titanium microstructure type found was a martensitic one, and in the gold palladium alloy, it presented a dendritic morphology. In titanium, the hardness in the base metal was 199 HV, smaller than the hardness in welding region, which was 421 HV, due to the presence of the martensitic microstructure. In the gold alloy, the hardness in the base metal was 196 HV, greater than the one found in the welding region, which was 103 HV, due to the dendritic microstructure. In the characterization of resistance to corrosion, the results showed a smaller resistance to the corrosion in the welding area for both biomaterials in the studied environment
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-08-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.