Thèse de Doctorat
DOI
10.11606/T.88.2004.tde-25072012-143154
Document
Auteur
Nom complet
Valdinei Ferreira da Silva
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2004
Directeur
Jury
Bose Filho, Waldek Wladimir (Président)
Andrade, Arnaldo Homobono Paes de
Araújo, José Alexander
Ferrante, Maurizio
Tarpani, José Ricardo
Titre en portugais
Comportamento da liga de alumínio A356-T6 fundida e tixoextrudada sob fadiga isotérmica e termomecânica
Mots-clés en portugais
Fadiga isotérmica
Fadiga termomecânica
Fundido
Liga de alumínio A356-T6
Processamento no estado semi-sólido
Tixoextrusão
Resumé en portugais
Gradientes térmicos induzidos no interior de componentes sujeitos a variações de temperatura durante o período de funcionamento podem provocar a ocorrência de tensões e deformações internas. A repetição destes ciclos térmicos pode causar a nucleação e a propagação de trincas por um processo denominado fadiga termomecânica. Este trabalho apresenta um estudo sobre o comportamento da liga de alumínio A356-T6, processada nas condições fundida e tixoextrudada, sob fadiga isotérmica e termomecânica. Foram realizados ensaios de fadiga de baixo ciclo isotérmica para as temperaturas de 120 e 280°C, e ensaios de fadiga termomecânica em-fase e fora-de-fase para a faixa de temperatura de 120 a 280°C. O material tixoextrudado apresentou melhor desempenho em fadiga nas condições isotérmica e anisotérmica (termomecânica) devido a uma microestrutura globular com menor nível de porosidade.
Titre en anglais
Casting and tixoextruded A356-T6 aluminum alloy behavior under isothermal and thermomechanical fatigue
Mots-clés en anglais
A356-T6 aluminum alloy
Casting
Fatigue
Isothernal fatigue
Semi-solid processing
Thermomechanical fatigue
Tixoextruded
Resumé en anglais
Thermal gradients induced in components during service under temperature changes can cause internal stresses and strains. This cyclic thermal behavior can cause crack nucleation and propagation under a process denominated thermomechanical fatigue. Permanent mold casting and tixoextruded A356-T6 aluminum alloy behavior under isothermal and thermomechanical fatigue was study in this work. Isothermal low cycle fatigue tests were performed in temperatures of 120 and 280°C. In-phase and out-of-phase thermomechanical fatigue tests were carried out in temperature range from 120 to 280°C. The tixoextruded material presented better isothermal and thermomechanical fatigue performance due to a globular microstructure and lower porosity level.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2012-07-25
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.