Tese de Doutorado
DOI
10.11606/T.88.2004.tde-25072012-143154
Documento
Autor
Nome completo
Valdinei Ferreira da Silva
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2004
Orientador
Banca examinadora
Bose Filho, Waldek Wladimir (Presidente)
Andrade, Arnaldo Homobono Paes de
Araújo, José Alexander
Ferrante, Maurizio
Tarpani, José Ricardo
Título em português
Comportamento da liga de alumínio A356-T6 fundida e tixoextrudada sob fadiga isotérmica e termomecânica
Palavras-chave em português
Fadiga isotérmica
Fadiga termomecânica
Fundido
Liga de alumínio A356-T6
Processamento no estado semi-sólido
Tixoextrusão
Resumo em português
Gradientes térmicos induzidos no interior de componentes sujeitos a variações de temperatura durante o período de funcionamento podem provocar a ocorrência de tensões e deformações internas. A repetição destes ciclos térmicos pode causar a nucleação e a propagação de trincas por um processo denominado fadiga termomecânica. Este trabalho apresenta um estudo sobre o comportamento da liga de alumínio A356-T6, processada nas condições fundida e tixoextrudada, sob fadiga isotérmica e termomecânica. Foram realizados ensaios de fadiga de baixo ciclo isotérmica para as temperaturas de 120 e 280°C, e ensaios de fadiga termomecânica em-fase e fora-de-fase para a faixa de temperatura de 120 a 280°C. O material tixoextrudado apresentou melhor desempenho em fadiga nas condições isotérmica e anisotérmica (termomecânica) devido a uma microestrutura globular com menor nível de porosidade.
Título em inglês
Casting and tixoextruded A356-T6 aluminum alloy behavior under isothermal and thermomechanical fatigue
Palavras-chave em inglês
A356-T6 aluminum alloy
Casting
Fatigue
Isothernal fatigue
Semi-solid processing
Thermomechanical fatigue
Tixoextruded
Resumo em inglês
Thermal gradients induced in components during service under temperature changes can cause internal stresses and strains. This cyclic thermal behavior can cause crack nucleation and propagation under a process denominated thermomechanical fatigue. Permanent mold casting and tixoextruded A356-T6 aluminum alloy behavior under isothermal and thermomechanical fatigue was study in this work. Isothermal low cycle fatigue tests were performed in temperatures of 120 and 280°C. In-phase and out-of-phase thermomechanical fatigue tests were carried out in temperature range from 120 to 280°C. The tixoextruded material presented better isothermal and thermomechanical fatigue performance due to a globular microstructure and lower porosity level.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2012-07-25
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.