Disertación de Maestría
DOI
10.11606/D.88.2004.tde-25092014-162218
Documento
Autor
Nombre completo
Luciano Henrique de Almeida
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2004
Director
Tribunal
Grandini, Carlos Roberto (Presidente)
Florêncio, Odila
Ishikawa, Tomaz Toshimi
Título en portugués
Reorientação induzida por tensão devido a oxigênio e nitrogênio em ligas de Nb-Ta
Palabras clave en portugués
Atrito interno
Espectroscopia anelástica
Gases em metais
Resumen en portugués
O estudo da interação de metais com impurezas intersticiais como oxigênio e nitrogênio em solução sólida tem despertado o interesse de pesquisadores de diversas áreas, pois tais impurezas modificam algumas propriedades mecânicas destes metais. A presença destes intersticiais causa um desvio na elasticidade perfeita, chamada anelasticidade. Estudos de espectroscopia anelástica nos fornecem informações a respeito do comportamento destas impurezas na matriz metálica. Nesta dissertação foram analisadas amostras policristalinas da liga Nb-8,9%p.Ta com diferentes concentrações de elementos intersticiais. Foram efetuadas medidas de espectroscopia anelástica utilizando um pêndulo torção invertido, operando com freqüência de 2,0 a 27,0 Hz, num intervalo de temperatura compreendido entre 300 a 700 K. Observamos a presença de estruturas de relaxação que foram atribuídas a processos de relaxação devido à reorientação induzida por tensão de átomos intersticiais em tomo de átomos da matriz metálica. Constatamos, também, a existência de uma relação entre a intensidade da estrutura de relaxação e a concentração de intersticiais. As estruturas de relaxação foram decompostas em seus picos constituintes, que nos permitiu identificar os seguintes processos de relaxação: Ta-O, Nb-O, Nb-O-O e Nb-N.
Título en inglés
Stress induced ordering due the oxygen and nitrogen in Nb-Ta alloys
Palabras clave en inglés
Anelastic spectroscopy
Gases in metaIs
Internal friction
Resumen en inglés
The study of the metal interaction with interstitial impurities as oxygen and nitrogen in solid solution has aroused the interest of researchers of diverse areas, therefore such impurities modify some mechanical properties of these metaIs. The presence of these interstitials causes a deviation in the perfect elasticity, called anelasticity. Studies of anelastic spectroscopy provide information of the behaviour of these impurities in the metallic matrix. In this dissertation, polycrystalline samples of Nb-8.9%p.Ta alloy have been analysed with different concentrations of interstitials elements. Measurements of anelastic spectroscopy were carried out using an inverted torsion pendulum, operating with frequency of 2.0 to 27.0 Hz and in a temperature range between 300 and 700 K. It was observed the presence of relaxation structures that have been attributed to stress induced ordering due to interstitial atoms around atoms of the metallic matrix. It is also evidenced the existence of a relation between the intensity of the relaxation's structures and the interstitials concentration. The relaxation structures have been decomposed in its constituents peaks, what it allowed to identify the following processes of relaxation: Ta-O, Nb-O, Nb-O-O and Nb-N.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-10-02
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.