Doctoral Thesis
DOI
10.11606/T.88.2003.tde-25102005-104002
Document
Author
Full name
João Adriano Rossignolo
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2002
Supervisor
Committee
Agnesini, Marcos Vinicio Costa (President)
Ferreira, Osny Pellegrino
Figueiredo Filho, Jasson Rodrigues de
Paulon, Vladimir Antonio
Souza, Milton Ferreira de
Title in Portuguese
"Concreto leve de alto desempenho modificado com SB para pré-fabricados esbeltos - dosagem, produção, propriedades e microestrutura"
Keywords in Portuguese
Concreto leve
concreto modificado com polímero
elementos pré-fabricados
microestrutura
Abstract in Portuguese
Esta tese aborda a aplicação da tecnologia dos concretos leves de alto desempenho (CLAD) para a produção de elementos construtivos esbeltos pré-fabricados, tais como painéis estruturais e de vedação e peças para cobertura, apresentando um concreto com propriedades especiais em função da utilização conjunta de látex de estireno butadieno (SB), sílica ativa, superplastificante acelerador e agregados leves nacionais, denominado concreto leve de alto desempenho modificado com SB. Desenvolveu-se um amplo programa experimental para a análise dos concretos, tendo como objetivos o estudo dos processos de dosagem e produção, caracterização das propriedades dos concretos nos estados fresco e endurecido, análise da ductilidade de elementos construtivos esbeltos pré-fabricados submetidos à flexão, assim como a obtenção de informações microestruturais sobre a matriz de cimento e a zona de transição entre o agregado e a matriz de cimento. Os resultados do programa experimental demonstraram que os concretos leves de alto desempenho modificados com SB são extremamente adequados à produção de elementos pré-fabricados esbeltos, devido essencialmente à redução da massa específica e ao excelente desempenho das propriedades relacionadas à resistência mecânica e durabilidade. Nos estudos microestruturais, observou-se que a utilização de sílica ativa e de SB promoveram a diminuição da quantidade e do diâmetro dos poros capilares e da quantidade de hidróxido de cálcio (CH) na matriz de cimento, assim como reduziram a espessura da zona de transição agregado-matriz. Observou-se, também, que os concretos com agregados leves nacionais apresentaram valores da espessura da zona de transição agregado-matriz inferiores aos observados para os concretos com agregados tradicionais.
Title in English
High performance latex-modified lightweight aggregate concrete for thin precast components - dosage, production, properties and microstructure
Keywords in English
Lightweight aggregates concrete
microstructure
polymer-modified concrete
precast elements
Abstract in English
This dissertation deals with the application of the high performance lightweight aggregate concrete (HPLWAC) for the production of thin precast components, such as structural and insulation panels and elements for covering. A concrete with special properties was presented, once the use of styrene-butadiene latex (SBR), silica fume, accelerating superplastificizer and Brazilian lightweight aggregates, named SBR-modified high performance lightweight aggregate concrete. Our main goals in the experimental program were the study of concrete dosage and production, the characterization of concretes properties, the thin precast components analysis, as well as the microstructural study about both cement paste and the interfacial transition zone (ITZ) between aggregate and cement paste. The main results show that the SBR-modified HPLWAC are extremely appropriate to the production of thin precast components, due essentially to the density reduction and to the high performance of mechanical and durability properties. Besides this, it was viewed that the silica fume and SBR use promote the decrease of the amount and diameter of the capillary pores, as well as the amount of calcium hydroxide (CH) in the cement paste. Additionally, they reduce the thickness of the interfacial transition zone between aggregate and cement paste. It was also observed that the concretes with Brazilian lightweight aggregate presented lower values of the interfacial transition zone thickness than the ones observed for the concretes with traditional aggregates (basalt).
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
teserossignolo.pdf (3.86 Mbytes)
Publishing Date
2005-10-26
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.