Thèse de Doctorat
DOI
10.11606/T.88.2003.tde-25102005-104002
Document
Auteur
Nom complet
João Adriano Rossignolo
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2002
Directeur
Jury
Agnesini, Marcos Vinicio Costa (Président)
Ferreira, Osny Pellegrino
Figueiredo Filho, Jasson Rodrigues de
Paulon, Vladimir Antonio
Souza, Milton Ferreira de
Titre en portugais
"Concreto leve de alto desempenho modificado com SB para pré-fabricados esbeltos - dosagem, produção, propriedades e microestrutura"
Mots-clés en portugais
Concreto leve
concreto modificado com polímero
elementos pré-fabricados
microestrutura
Resumé en portugais
Esta tese aborda a aplicação da tecnologia dos concretos leves de alto desempenho (CLAD) para a produção de elementos construtivos esbeltos pré-fabricados, tais como painéis estruturais e de vedação e peças para cobertura, apresentando um concreto com propriedades especiais em função da utilização conjunta de látex de estireno butadieno (SB), sílica ativa, superplastificante acelerador e agregados leves nacionais, denominado concreto leve de alto desempenho modificado com SB. Desenvolveu-se um amplo programa experimental para a análise dos concretos, tendo como objetivos o estudo dos processos de dosagem e produção, caracterização das propriedades dos concretos nos estados fresco e endurecido, análise da ductilidade de elementos construtivos esbeltos pré-fabricados submetidos à flexão, assim como a obtenção de informações microestruturais sobre a matriz de cimento e a zona de transição entre o agregado e a matriz de cimento. Os resultados do programa experimental demonstraram que os concretos leves de alto desempenho modificados com SB são extremamente adequados à produção de elementos pré-fabricados esbeltos, devido essencialmente à redução da massa específica e ao excelente desempenho das propriedades relacionadas à resistência mecânica e durabilidade. Nos estudos microestruturais, observou-se que a utilização de sílica ativa e de SB promoveram a diminuição da quantidade e do diâmetro dos poros capilares e da quantidade de hidróxido de cálcio (CH) na matriz de cimento, assim como reduziram a espessura da zona de transição agregado-matriz. Observou-se, também, que os concretos com agregados leves nacionais apresentaram valores da espessura da zona de transição agregado-matriz inferiores aos observados para os concretos com agregados tradicionais.
Titre en anglais
High performance latex-modified lightweight aggregate concrete for thin precast components - dosage, production, properties and microstructure
Mots-clés en anglais
Lightweight aggregates concrete
microstructure
polymer-modified concrete
precast elements
Resumé en anglais
This dissertation deals with the application of the high performance lightweight aggregate concrete (HPLWAC) for the production of thin precast components, such as structural and insulation panels and elements for covering. A concrete with special properties was presented, once the use of styrene-butadiene latex (SBR), silica fume, accelerating superplastificizer and Brazilian lightweight aggregates, named SBR-modified high performance lightweight aggregate concrete. Our main goals in the experimental program were the study of concrete dosage and production, the characterization of concretes properties, the thin precast components analysis, as well as the microstructural study about both cement paste and the interfacial transition zone (ITZ) between aggregate and cement paste. The main results show that the SBR-modified HPLWAC are extremely appropriate to the production of thin precast components, due essentially to the density reduction and to the high performance of mechanical and durability properties. Besides this, it was viewed that the silica fume and SBR use promote the decrease of the amount and diameter of the capillary pores, as well as the amount of calcium hydroxide (CH) in the cement paste. Additionally, they reduce the thickness of the interfacial transition zone between aggregate and cement paste. It was also observed that the concretes with Brazilian lightweight aggregate presented lower values of the interfacial transition zone thickness than the ones observed for the concretes with traditional aggregates (basalt).
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
teserossignolo.pdf (3.86 Mbytes)
Date de Publication
2005-10-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.