Dissertação de Mestrado
DOI
10.11606/D.88.1998.tde-25112014-155350
Documento
Autor
Nome completo
Washington Luiz Esteves Magalhães
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1998
Orientador
Banca examinadora
Souza, Milton Ferreira de (Presidente)
Lahr, Francisco Antonio Rocco
Leão, Alcides Lopes
Título em português
Impregnação de Pinus Caribaea Hondurensis com álcool furfurílico e tetra-etil-ortosilicato
Palavras-chave em português
Impregnação
Madeira
Modificação química
Resumo em português
Pinus caribeae hondurensis foi impregnado pelo processo vácuo/pressão, com tetra etil ortosilicato (TEOS) e álcool furfurílico (FFA). Os reagentes foram introduzidos com seus respectivos catalisadores ácidos, e após aquecimento promoveu-se a polimerização no interior da madeira. Os métodos de caracterização utilizados foram a difração de raios-X, a microscopia eletrônica, a espectroscopia de infravermelho e a ressonância nuclear magnética de sólido. O tratamento com TEOS trouxe pequenas melhorias na resistência mecânica e na estabilidade dimensional da madeira. Houve formação do gel de TEOS entre as cadeias de celulose com diminuição de sua cristalinidade. Foram analisadas as causas da perda de resistência mecânica e aumento da estabilidade dimensional da madeira tratada com FFA. A madeira impregnada com FFA apresentou aumento da cristalinidade da celulose e comportamento frágil na fratura. A resina de FFA não preenche o lúmem das células da madeira, mas reage com os sítios OH e deposita-se na superficie das paredes celulares. O duplo tratamento, primeiramente com TEOS e depois com FFA, melhora a estabilidade dimensional sem diminuir a resistência mecânica da madeira
Título em inglês
Pinus Caribaea Hondurensis infused with furfuryl alcohol and tetra ethyl orthosilicate
Palavras-chave em inglês
Chemical change
Infusing
Wood
Resumo em inglês
Pinus caribeae hondurensis was infused with tetra ethyl orthosilicate (TEOS) and furfuryl alcohol (FFA) using the vacuum/pressure processing. The reagents were instilled together with theirs acidic catalysts. After heat processing, the reaction was started within the wood. The characterization was carried out using of x-ray diffraction, scanning electron microscopy, infrared spectroscopy and solid state nuclear magnetic resonance. Infusing wood with TEOS leads to slight enhancements of the mechanical resistance and dimensional stability. Gel from TEOS reactions was formed between the cellulose chains with decrease of cristalinity. The causes of mechanical resistance lowering and dimensional stability increase were analyzed in wood treated with FFA. FFA instilled wood showed increased cellulose cristalline ordering and also fragile fracture behavior. FFA resin did not soak into the wood cell lumen, but reacted with OH sites and covered the cell wall surfaces. Double treated wood, first with TEOS and later with FFA, had the dimensional stability improved without decrease in mechanical resistance
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2014-11-26
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.