Tesis Doctoral
DOI
10.11606/T.88.2016.tde-26092016-095442
Documento
Autor
Nombre completo
Isabel Cristina Buttignon
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2001
Director
Tribunal
Gomes, Samuel Irati Novaes (Presidente)
Ishikawa, Tomaz Toshimi
Bose Filho, Waldek Wladimir
Kobayashi, Yukio
Souza, Paulo Cézar Rioli Duarte de
Título en portugués
Efeitos do fluxo ativado como recebido na soldagem a arco submerso com adição de pó de ferro
Palabras clave en portugués
Adição de pó de ferro
Arco submerso
Microestruturas
Propriedades mecânicas
Resumen en portugués
O objetivo deste trabalho foi estudar as propriedades mecânicas do metal como soldado usando fluxo ativado na condição como recebido. Foram utilizadas cinco chapas base, sendo quatro delas de aço do tipo alta resistência e baixa liga (ABRL) e uma de aço carbono comum SAE 1020, que foram soldadas usando um único passe. O eletrodo utilizado foi o arame EM 12K , diâmetro de 4 mm e pó de ferro 400. As condições de soldagem utilizada foram: tensão de 34V, corrente de 660A, velocidade de soldagem de 30 cm/mim por minuto e uma adição de pó metálico de 373 g/m. Estas condições produzem um aporte de calor de 4,5 kJ/mm e uma diluição da chapa base em torno de 43%. Os ensaios mecânicos realizados forma de dureza, de tração e de impacto. A natureza das inclusões não metálicas foi investigada por microscopia eletrônica de varredura e análise por Energy Dispersive X RAY (EDS). Os resultados mostraram que as condições do fluxo e a diluição da chapa base alteraram a química nos metais como soldados, principalmente o oxigênio, isto permitiu mudanças significativas na temperabilidade. Como resultado as percentagens das microestruturas foram bastante alteradas principalmente na ferrita acicular, ocasionando mudanças nas propriedades mecânicas de dureza, tração e impacto.
Título en inglés
not available
Palabras clave en inglés
Metal mechanical properties
Microstructures
Submerged arc
Resumen en inglés
The objective of this work was to study the properties of the metal as welded using activated flux in the condition as received. Five base plates, four of which were HSLA steel and one SAE 1020, that were welded using a single pass. EM 12K electrode and 400 metallic powder were used. The conditions for welding were: voltage 34V, current 660A, welding speed 30 cm/min and addition of metallic powder 373 Kg/M. These conditions produced a heat input of 4,5 kJ/mm and dilution in the base plate around 43%. Mechanical tests of hardness, impact resistance and tensile strength were carried out. The nature of non-metallic inclusions was investigated by scanning electron microscopy and analysis by Energy Dispersive X-Ray (EDS). The results showed that the conditions of the flux and the dilution of the base plate changed the chemical compositions in the metal as welded, mainly oxygen, which altered significantly the hardenability. As a result, the percentage of the microstructures changed, specially for acicular ferrite, allowing for changes in mechanical properties of hardness, impact resistance and tensile strength.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-09-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.