Thèse de Doctorat
DOI
10.11606/T.88.2016.tde-26092016-095442
Document
Auteur
Nom complet
Isabel Cristina Buttignon
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2001
Directeur
Jury
Gomes, Samuel Irati Novaes (Président)
Ishikawa, Tomaz Toshimi
Bose Filho, Waldek Wladimir
Kobayashi, Yukio
Souza, Paulo Cézar Rioli Duarte de
Titre en portugais
Efeitos do fluxo ativado como recebido na soldagem a arco submerso com adição de pó de ferro
Mots-clés en portugais
Adição de pó de ferro
Arco submerso
Microestruturas
Propriedades mecânicas
Resumé en portugais
O objetivo deste trabalho foi estudar as propriedades mecânicas do metal como soldado usando fluxo ativado na condição como recebido. Foram utilizadas cinco chapas base, sendo quatro delas de aço do tipo alta resistência e baixa liga (ABRL) e uma de aço carbono comum SAE 1020, que foram soldadas usando um único passe. O eletrodo utilizado foi o arame EM 12K , diâmetro de 4 mm e pó de ferro 400. As condições de soldagem utilizada foram: tensão de 34V, corrente de 660A, velocidade de soldagem de 30 cm/mim por minuto e uma adição de pó metálico de 373 g/m. Estas condições produzem um aporte de calor de 4,5 kJ/mm e uma diluição da chapa base em torno de 43%. Os ensaios mecânicos realizados forma de dureza, de tração e de impacto. A natureza das inclusões não metálicas foi investigada por microscopia eletrônica de varredura e análise por Energy Dispersive X RAY (EDS). Os resultados mostraram que as condições do fluxo e a diluição da chapa base alteraram a química nos metais como soldados, principalmente o oxigênio, isto permitiu mudanças significativas na temperabilidade. Como resultado as percentagens das microestruturas foram bastante alteradas principalmente na ferrita acicular, ocasionando mudanças nas propriedades mecânicas de dureza, tração e impacto.
Titre en anglais
not available
Mots-clés en anglais
Metal mechanical properties
Microstructures
Submerged arc
Resumé en anglais
The objective of this work was to study the properties of the metal as welded using activated flux in the condition as received. Five base plates, four of which were HSLA steel and one SAE 1020, that were welded using a single pass. EM 12K electrode and 400 metallic powder were used. The conditions for welding were: voltage 34V, current 660A, welding speed 30 cm/min and addition of metallic powder 373 Kg/M. These conditions produced a heat input of 4,5 kJ/mm and dilution in the base plate around 43%. Mechanical tests of hardness, impact resistance and tensile strength were carried out. The nature of non-metallic inclusions was investigated by scanning electron microscopy and analysis by Energy Dispersive X-Ray (EDS). The results showed that the conditions of the flux and the dilution of the base plate changed the chemical compositions in the metal as welded, mainly oxygen, which altered significantly the hardenability. As a result, the percentage of the microstructures changed, specially for acicular ferrite, allowing for changes in mechanical properties of hardness, impact resistance and tensile strength.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-09-26
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.