Disertación de Maestría
DOI
10.11606/D.88.2005.tde-27042015-162102
Documento
Autor
Nombre completo
Waldemar Thomazini Neto
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2005
Director
Tribunal
Messaddeq, Younes (Presidente)
Martines, Marco Antonio Utrera
Mastelaro, Valmor Roberto
Título en portugués
Preparação e caracterização estrutural de vidros fosfato dopados com érbio
Palabras clave en portugués
Não disponível
Resumen en portugués
Os vidros fosfatos são bem conhecidos pela facilidade de sua formação vítrea. Assim, estes vidros despertam interesse seja para estudos acadêmicos ou aplicações tecnológicas. Deste modo, no presente trabalho buscou-se explorar as propriedades ópticas de uma matriz a base de fosfatos contendo alta concentração de íon Er3+. Em uma primeira etapa, em amostras vítreas conteúdo 4% mol de Er2O3, avaliou-se o efeito de incorporação da concentração de Al2O3. Assim, determinou-se as suas temperaturas características dos vidros, o tempo de vida experimental e calculado, o índice de refração, densidade, espectros na região do infravermelho e espectros de absorção na região do UV-Vis. Os tempos de vida teóricos foram obtidos utilizando os cálculos de Judd-Ofelt, para posteriormente poder serem comparados com os tempos de vida experimentais e avaliar a solubilidade do íon érbio. Nesta etapa também foi possível de se reproduzir a amostra 5 % de Al2O3 em câmara seca e observar a influência da água sobre as propriedades descritas acima. Em uma segunda etapa foram preparadas matrizes de fosfato que apresentassem na sua maioria a estrutura ortofosfato. Amostras com diferentes concentrações de íon érbio foram preparados. As características térmicas e ópticas foram determinadas como foi também explorado as propriedades estruturais dos vidros conteúdo 1 e 2 % de Er2O3.
Título en inglés
Not avilable
Palabras clave en inglés
Not available
Resumen en inglés
Phosphate glasses are very good as glass forming system. These glasses have attracted considerable interest because of their scientific and technological importance. In this work we investigated the optical properties of phosphate glasses having a high concentration of Er3+ ion. In a first step, the effect of incorporation of Al2O3 was studied in samples having Er2O3 (4% mol). In this way, their characteristics temperatures, life time, refraction index, density, infrared measurements and Uv-Vis absorption spectra are measured. Judd-Ofelt data was used to determine the lifetime values and to estimate the erbium ions solubility. The sample contain Al2O3 (5% mol) was prepared in a dry box and the influence of water was also studied in the above mentioned properties. The second step was focus in prepared phosphate glasses matrix that has an ortophophate structure. The thermal and optical properties were measured in function of Er concentration. The structural properties of glass containing Er2O3 (1 and 2% mol) were determined
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-05-04
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.