Tesis Doctoral
DOI
10.11606/T.88.1996.tde-29012010-160947
Documento
Autor
Nombre completo
Samuel Jose Casarin
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1996
Director
Tribunal
Rollo, Joao Manuel Domingos de Almeida (Presidente)
Goldenstein, Helio
Gregolin, José Ângelo Rodrigues
Mei, Paulo Roberto
Spinelli, Dirceu
Título en portugués
Caracterização da temperabilidade de um aço C-Mn microligado ao boro, através de dilatometria e curvas de transformações de fases por resfriamento contínuo.
Palabras clave en portugués
Aços ao boro
Curvas CCT
Dilatometria
Transformações de fases
Resumen en portugués
No presente trabalho, foi realizado um estudo sobre a influência da adição do boro em um aço C-Mn, nas transformações de fases por resfriamento contínuo, através da técnica dilatométrica. Para este estudo, utilizou-se dois aços de composição química semelhante: o aço 10B22 com 30 ppm de boro e o aço sem boro é o E1522, equivalente. Foram traçadas as curvas de CCT dos dois aços, onde analisou-se o efeito de temperabilidade do boro através das curvas de resfriamento. Os materiais foram ensaiados em um dilatômetro de resfriamento rápido, utilizando corpos de prova cilíndricos, resfriados por injeção de ar e hélio. Os resultados gráficos dos processos de resfriamento foram comparados com análises metalográficas ótica estruturais e quantitativas e também por medidas de dureza. Detalhes microestruturais, tais como, contagem de fases formadas em função das taxas de resfriamento, tamanho de grão, distribuição de inclusões e precipitados, foram extraídos, através de um sistema de análise de imagens. Complementando o trabalho, foi realizado uma completa documentação fotográfica das microestruturas, com uma indicação final do tratamento térmico mais adequado aos aços C-Mn microligados ao boro.
Título en inglés
C-Mn boron microalloyed steel hardenability characterization throught dilatometry and continuous cooling transformations curves.
Palabras clave en inglés
Boron steels
CCT curves
Dilatometry
Phase transformation
Resumen en inglés
This work presents a study about the influence of boron on phase transformation by continuous cooling in a C-Mn steel using the dilatometric technique. For this study two close chemical composition steels were applied: a 10B2 steel with 30 ppm of boron and a E1522 steel without boron. For both steels the CCT curves were obtained, where the effect of boron on hardenability was analysed throughout continuous cooling curves. Both materials were testedcin a high speed quenching dilatometer, using cilindricals samples quenched by helium blow on their surfaces. The graphics results of cooling processes were compared with microstructural and quantitative optical metallographic analysis and hardness measurements. Microstructural features as such phases fraction as a function of cooling rates, grain size, and distributions of inclusions and precipitates were obtained through an image analysis system. In addition, complete microstructural photography documentation was carried out where it was possible to indicate the best heat treatment to boron microalloyed C-Mn steels.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
SamuelJoseCasarinD.pdf (16.89 Mbytes)
Fecha de Publicación
2010-02-23
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.