Tese de Doutorado
DOI
https://doi.org/10.11606/T.97.2013.tde-08102013-084019
Documento
Autor
Nome completo
Felipe Antunes Santos
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2013
Orientador
Banca examinadora
Santos, Claudinei dos (Presidente)
Castanho, Sonia Regina Homem de Mello
Conte, Rosa Ana
Elias, Carlos Nelson
Nunes, Carlos Angelo
Título em português
Vitrocerâmica à base de silicato de lítio para uso como material dentário utilizando casca de arroz como fonte alternativa de silica
Palavras-chave em português
biomateriais
cristalização
materiais dentários
silicatos
Vidro cerâmico
Resumo em português
O presente trabalho sugere a substituição da sílica comercial pela sílica obtida da casca de arroz como fonte alternativa para obtenção do dissilicato de lítio, material que pode ser utilizado em aplicações odontológicas. Para esse fim foram desenvolvidos materiais com estequiometria base de 33,33%mol. Li2O e 66,67%mol. SiO2 com e sem adição de óxidos complementares, visando à obtenção de vitrocerâmicas de maior tenacidade, por meio das duas fontes de sílica, comercial e da casca de arroz. Como caracterizações iniciais, foram realizadas difrações de raios X (DRX) para as misturas iniciais das matérias-primas antes e após a fusão para obtenção dos vidros. Para o caso dos materiais sem adição dos óxidos, a caracterização quanto à sua devitrificação, foi realizada por análise térmica diferencial (ATD), utilizando diferentes taxas de aquecimento e granulometrias, para ambas as fontes de sílica. Valores de temperatura de pico de cristalização (Tp), sem adição dos óxidos, ficaram na faixa de 640°C para os materiais de ambas as fontes de sílica. Também por ATD foi analisado o fenômeno de devitrificação dos materiais com adição dos óxidos. Além disso, para observar a existência de fases intermediárias no sistema, foram também realizadas análises por DRX com variação térmica. Para visualizar a alteração microestrutural, de acordo com a variação da temperatura de tratamento térmico (TT), fonte de sílica e influência dos óxidos, foram realizadas caracterizações por microscopia eletrônica de varredura (MEV). O comportamento citotóxico dos materiais frente às colônias celulares foi observado por meio do ensaio de citotoxicidade. As propriedades mecânicas, de acordo com as alterações das variáveis estudadas, foram obtidas por meio de cálculos de dureza e tenacidade à fratura por ensaio Vickers. Foram encontrados valores de tenacidade à fratura de aproximadamente 1,75 MPam1/2 para ambas as fontes de sílica, com adição de óxidos a 660°C (TT). Diante dos resultados obtidos é possível afirmar grande potencialidade na substituição da sílica comercial pela sílica da casca de arroz.
Título em inglês
Lithium disilicate glass-ceramic used as dental material with silica from rice husk, an alternative source
Palavras-chave em inglês
biomaterials
crystallization
dental materials
Glass-ceramic
silicates
Resumo em inglês
This work suggests the replacement of commercial silica by silica obtained from rice husk as alternative source for obtaining lithium disilicate material that can be used in dental application. The lithium disilicate as dental material is a glass-ceramic that has good mechanical properties and chemical stability. For these developments the materials have been obtained using stoichiometry of 33.33%mol. Li2O and 66.67%mol. SiO2, without complementary oxide addition or with, seeking better fracture toughness comportment, to both sources of silica, commercial and from rice husk. As initial characterization X-ray diffraction (XRD) was performed for the mixtures of materials before and after the fusion to obtain the glasses. For materials without oxide addition, the two materials developed were characterized for their devitrification, in other words, the transition from glass to glass-ceramic was observed by differential thermal analysis (DTA), using different heating rates and granulometries. Peak crystallization temperatures (Tp), to both silica sources, heat rate 10°C/min and 1mm of granulometry, was in average values of 640°C. The DTA was used to verify the devitrification in material with oxide addition too. In addition, to observe the possible formation of intermediate phases on stoichiometric system of lithium disilicate, were also carried out high temperature X-ray diffractomery (HTXRD). To view the microstructural changes occurring in the system, according to the variation of heat treatments temperatures (HT), silica source and oxides influence, characterizations were performed by scanning electron microscopy (SEM). The cytotoxic behavior of the materials in cell colonies was observed by the cytotoxicity test. Mechanical properties, Vickers hardness and fracture toughness, were determined by calculus, using Vickers test data. Values of approximately 1.75 MPam½ were obtained for both silica sources with oxide addition to 660°C (HT). Results obtained show great potential in the replacement of commercial silica by rice husk silica.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMT13002_C.pdf (10.15 Mbytes)
Data de Publicação
2013-10-08
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.