• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tese de Doutorado
DOI
10.11606/T.97.2017.tde-06022017-104515
Documento
Autor
Nome completo
Henrique Varella Ribeiro
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2016
Orientador
Banca examinadora
Baptista, Carlos Antonio Reis Pereira (Presidente)
Faria, Maria Ismenia Sodero Toledo
Marcomini, José Benedito
Tosetti, João Pedro Valls
Voorwald, Herman Jacobus Cornelis
Título em português
Caracterização microestrutural e mecânica de juntas soldadas a laser em um aço ARBL
Palavras-chave em português
caracterização mecânica
caracterização microestrutural
Soldagem a laser
tenacidade à fratura e propagação de trincas por fadiga
Resumo em português
Os aços de alta resistência e baixa liga (ARBL) são amplamente empregados nas indústrias automotiva, petrolífera e naval por apresentarem boas propriedades mecânicas e boa soldabilidade. A seleção do processo de soldagem utilizado para a fabricação de componentes depende de vários fatores, entre eles a qualidade do cordão de solda e a capacidade de produção, ambas obtidas ao se utilizar a soldagem a laser, processo que vem sendo cada vez mais utilizado nas indústrias. As propriedades dos cordões de solda são afetadas pelo processo de soldagem e pelos parâmetros do processo, e o conhecimento do desempenho mecânico do cordão de solda é essencial para garantir a confiabilidade da união soldada. A caracterização mecânica de cordões de solda é complexa devido aos diversos fatores que podem afetá-lo, como as alterações metalúrgicas, diferentes propriedades mecânicas nas regiões do cordão de solda, presença de descontinuidades, tensão residual e complexo estado de tensão devido à geometria da junta. O presente trabalho obteve uniões entre chapas de aço ARBL pelo processo a laser em duas condições diferentes: com alto aporte térmico e baixo aporte térmico. A utilização de diferentes aportes térmicos gerou cordões de solda com microestruturas distintas, e avaliou-se, deste modo, o comportamento mecânico associando-o à microestrutura gerada. Para a avaliação da microestrutura utilizou-se da microscopia óptica e eletrônica de varredura, e para a caracterização mecânica empregou-se a aferição da dureza, ensaio de tração, ensaio de tenacidade à fratura, avaliada pelo CTOD, e ensaio de propagação da trinca por fadiga. Devido às alterações metalúrgicas causadas pelos diferentes aportes térmicos verificou-se diferente comportamento mecânico entre os cordões de solda em função da microestrutura obtida.
Título em inglês
Microstructural and mechanical characterization of laser welded joints on a HSLA steel
Palavras-chave em inglês
fracture toughness and fatigue cracks propagation
Laser welding
mechanical characterization
microstructural characterization
Resumo em inglês
High-strength low-alloy steels (HSLA) are widely used in the automotive and oil industries due to their good mechanical properties and good weldability. The selection of the welding process used to manufacture components depends on several factors, including the quality of the weld bead and the production capacity, both obtained when using laser welding, a process, which is being increasingly used in the industries. The weld beads properties are affected by the welding process and by its parameters, and the knowledge of the weld bead mechanical performance is essential to ensure the reliability of the welded joint. The weld beads mechanical characterization is complex due to various factors that may affect it, such as metallurgical changes, different mechanical properties in the regions of the weld bead, presence of discontinuities, residual stress and complex state of tension due to the geometry of the joint. The present work obtained the joining of HSLA steel sheets by laser process in two different conditions, with high heat input and low heat input. The use of different heat inputs produced weld beads with different microstructures; therefore, the welded joints were evaluated according to their mechanical behavior, relating it with the microstructural generated. For the microstructure evaluation, optical microscopy and scanning electron microscopy were used, and for the mechanical characterization hardness determination, tensile test, fracture toughness test (evaluated by CTOD) and fatigue crack propagation were performed. Due to the metallurgical changes caused by the different heat inputs, a different mechanical behavior was observed between the weld beads as a function of the microstructure obtained.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMT16002_C.pdf (11.56 Mbytes)
Data de Publicação
2017-02-06
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.