• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Dissertação de Mestrado
DOI
Documento
Autor
Nome completo
Julio Cesar Pereira dos Santos
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2018
Orientador
Banca examinadora
Coelho, Gilberto Carvalho (Presidente)
Ferreira, Flávio
Avillez, Roberto Ribeiro de
Gama, Sergio
Título em português
Seção isotérmica a 1200 °C e avaliação termodinâmica preliminar do sistema Al-Nb-V
Palavras-chave em português
Ligas de alta entropia
Metais refratários
Método Calphad
Sistema Al-Nb-V
Resumo em português
Um novo conceito para o desenvolvimento de ligas metálicas vem sendo estudado pela comunidade científica nos últimos anos, trata-se de ligas com elementos multiprincipais, também conhecidas como ligas de alta entropia (HEAs). HEAs constituídas de metais refratários e alumínio se destacam como possíveis ligas para utilização na indústria aeroespacial por apresentaram alta resistência específica. Dessa forma, torna-se necessário uma investigação das relações de fases envolvendo metais refratários e o alumínio. Para este trabalho, foi escolhido o sistema Al-Nb-V, uma vez que se encontrou apenas uma seção isotérmica experimental completa do sistema e nenhuma avaliação termodinâmica na literatura. Para o desenvolvimento do trabalho, foram produzidas ligas por fusão a arco. As amostras foram tratadas a 1200 °C por 10 dias para a determinação da seção isotérmica do sistema nessa temperatura. A caracterização microestrutural foi realizada por meio de difração de raios X (DRX), microscopia eletrônica de varredura (MEV) e microanálise eletrônica (EDS). Em relação à seção isotérmica disponível na literatura, foram observadas algumas diferenças. A seção da literatura, por exemplo, propõe a estabilidade do composto ternário NbVAl2, o qual não foi encontrado neste trabalho. Os resultados permitiram a determinação de boa parte da seção isotérmica a 1200 °C do sistema Al-Nb-V. Em paralelo, foi realizada uma revisão das avaliações termodinâmicas dos binários disponíveis na literatura. Os dados da literatura e os resultados experimentais obtidos foram utilizados para construir uma base de dados termodinâmicos pelo método Calphad. A modelagem termodinâmica apresenta boa consistência com os resultados experimentais obtidos.
Título em inglês
Isothermal section at 1200 °C and preliminary thermodynamic evaluation of the Al-Nb-V system
Palavras-chave em inglês
Al-Nb-V system
Calphad method
High entropy alloys
Refractory metals
Resumo em inglês
A new concept for the development of metallic alloys has been studied by the scientific community in recent years, which deals with multi-principal element alloys, also known as High Entropy Alloys (HEAs). HEAs with refractory metals and aluminium as constituents are possible alloys for use in the aerospace industry mainly due to their high specific resistance. In this way, the investigation of phase equilibria involving refractory metals and aluminium is required. For this work, the Al-Nb-V system was chosen, since only one complete experimental isothermal section of this system and no thermodynamic assessments were found in the literature. For the development of this work, 23 alloys were produced by arc melting. The alloys were treated at 1200 °C for 10 days to determine the isothermal section of the system at this temperature. The microstructural characterization was performed via X-ray diffractometry (XRD) scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). Some discrepancies were observed between the isothermal section available in the literature and the results of the present work. The isothermal section found in the literature, for example, proposes the stability of the ternary compound NbVAl2, which was not found in this work. Based on the present work, a new isothermal section at 1200 °C is proposed for the Al-Nb-V system. Also, a review of the thermodynamic descriptions of the binary systems available in the literature was performed. The literature data and the experimental results were used to build a thermodynamic database using the Calphad method. This preliminary thermodynamic modelling shows good consistency with the experimental results.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD18002_O.pdf (4.58 Mbytes)
Data de Publicação
2019-07-12
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.