Disertación de Maestría
DOI
10.11606/D.97.2016.tde-19092016-105938
Documento
Autor
Nombre completo
Sara de Carvalho Zago
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2015
Director
Tribunal
Vernilli Junior, Fernando (Presidente)
Justus, Sérgio Murilo
Silva, Sidiney Nascimento
Título en portugués
Estudo do efeito da cristalinidade da escória de aciaria nas propriedades físico-químicas do cimento Portland CPIII
Palabras clave en portugués
cimento Portland
Escorias de aciaria
propriedades fisicas
Resumen en portugués
O uso de escoria de aciaria, principal subproduto das industrias siderúrgicas do processo de conversão do ferro gusa em aço, como matéria-prima na produção de cimento Portland a partir de substituições de parte da escoria de alto forno, apresenta benefícios econômicos e ecológicos, visto que um resíduo industrial tornar-se-á matéria-prima na fabricação do cimento, reduzindo custo de energia, material e depósitos para estocagem de resíduos. Para tal estudo, a escória de aciaria foi submetida a refusão e a diferentes taxas resfriamento, com o objetivo de formar escorias com diferentes graus de cristalinidade. Após resfriamento foram conformados corpos de prova com adição ao cimento Portland de 0; 1,8; 3,6 e 5,4% em peso de escoria de aciaria. Foram determinados tempo de início e final pega, resistência a compressão após 3, 7, 28 e 91 dias da conformação dos corpos de prova, expansibilidade a quente e a frio. Os resultados confirmam que a escória de aciaria apresenta potencial para ser utilizada na indústria cimenteira. A verificação da influência da adição das escorias dará suporte para a Companhia Siderúrgica Nacional (CSN) decidir quanto a viabilidade da mudança do processo atual de resfriamento e quanto a destinação do resíduo.
Título en inglés
Study of the effect of steel slag crystallinity on the slag-blended cement physicochemical properties
Palabras clave en inglés
physical properties
Portland cement
steelmaking slag
Resumen en inglés
The use of steel slag, the main byproduct of the steel industries of the process of converting pig iron into steel as raw material for the production of Portland cement by replacing part of blast furnace slag, offering economic and ecological benefits, as that an industrial - waste becomes the raw material in cement production, reducing energy costs, equipment and tanks for storage of waste. For this study, steel slag was subjected to remelting and cooled at different rates, with the goal of forming slag with different degrees of crystallinity. After cooling, specimens with addition to Portland cement of 0, 1,8; 3,6 and 5,4% steel slag were conformed. Were determined the start time and end handle, compressive strength after 3, 7, 28 and 91 days of conformation, hot and cold expandability. The results confirm that the steel slag has the potential to be used in the cement industry. The verification of the influence of the addition of slag will support the National Steel Company (CSN) on the feasibility of changing the current cooling process and the allocation of the new waste.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD15004_O.pdf (7.76 Mbytes)
Fecha de Publicación
2016-09-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.