Mémoire de Maîtrise
DOI
10.11606/D.97.2016.tde-19092016-105938
Document
Auteur
Nom complet
Sara de Carvalho Zago
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2015
Directeur
Jury
Vernilli Junior, Fernando (Président)
Justus, Sérgio Murilo
Silva, Sidiney Nascimento
Titre en portugais
Estudo do efeito da cristalinidade da escória de aciaria nas propriedades físico-químicas do cimento Portland CPIII
Mots-clés en portugais
cimento Portland
Escorias de aciaria
propriedades fisicas
Resumé en portugais
O uso de escoria de aciaria, principal subproduto das industrias siderúrgicas do processo de conversão do ferro gusa em aço, como matéria-prima na produção de cimento Portland a partir de substituições de parte da escoria de alto forno, apresenta benefícios econômicos e ecológicos, visto que um resíduo industrial tornar-se-á matéria-prima na fabricação do cimento, reduzindo custo de energia, material e depósitos para estocagem de resíduos. Para tal estudo, a escória de aciaria foi submetida a refusão e a diferentes taxas resfriamento, com o objetivo de formar escorias com diferentes graus de cristalinidade. Após resfriamento foram conformados corpos de prova com adição ao cimento Portland de 0; 1,8; 3,6 e 5,4% em peso de escoria de aciaria. Foram determinados tempo de início e final pega, resistência a compressão após 3, 7, 28 e 91 dias da conformação dos corpos de prova, expansibilidade a quente e a frio. Os resultados confirmam que a escória de aciaria apresenta potencial para ser utilizada na indústria cimenteira. A verificação da influência da adição das escorias dará suporte para a Companhia Siderúrgica Nacional (CSN) decidir quanto a viabilidade da mudança do processo atual de resfriamento e quanto a destinação do resíduo.
Titre en anglais
Study of the effect of steel slag crystallinity on the slag-blended cement physicochemical properties
Mots-clés en anglais
physical properties
Portland cement
steelmaking slag
Resumé en anglais
The use of steel slag, the main byproduct of the steel industries of the process of converting pig iron into steel as raw material for the production of Portland cement by replacing part of blast furnace slag, offering economic and ecological benefits, as that an industrial - waste becomes the raw material in cement production, reducing energy costs, equipment and tanks for storage of waste. For this study, steel slag was subjected to remelting and cooled at different rates, with the goal of forming slag with different degrees of crystallinity. After cooling, specimens with addition to Portland cement of 0, 1,8; 3,6 and 5,4% steel slag were conformed. Were determined the start time and end handle, compressive strength after 3, 7, 28 and 91 days of conformation, hot and cold expandability. The results confirm that the steel slag has the potential to be used in the cement industry. The verification of the influence of the addition of slag will support the National Steel Company (CSN) on the feasibility of changing the current cooling process and the allocation of the new waste.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD15004_O.pdf (7.76 Mbytes)
Date de Publication
2016-09-19
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.