Dissertação de Mestrado
DOI
10.11606/D.97.2008.tde-20082013-155232
Documento
Autor
Nome completo
José Mauro Moraes Junior
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2008
Orientador
Banca examinadora
Nunes, Carlos Angelo (Presidente)
Guimarães, Valdir Alves
Barboza, Miguel Justino Ribeiro
Título em português
Influência do tratamento térmico de alívio de tensões pós-soldagem na microestrutura e comportamento mecânico de soldas produzidas com arame tubular rutílico
Palavras-chave em português
Alívio de tensões
Arame tubular rutílico
Microestrutura
Tenacidade ao impacto
Resumo em português
O objetivo desta Dissertação foi analisar o efeito do tratamento térmico de alívio de tensões pós-soldagem sobre a microestrutura e comportamento mecânico de soldas produzidas com arame tubular rutílico AWS E-81T1 Ni1. Foi soldada uma junta com 60 mm de espessura, na posição vertical e progressão ascendente. Esta junta foi dividida em três partes, sendo uma mantida como soldada e as outras duas tratadas termicamente por 6 horas em diferentes temperaturas, 585 °C e 650 °C. Avaliou-se o efeito do tratamento térmico sobre as propriedades mecânicas por meio de ensaio de dureza, tração e impacto Charpy-V. A caracterização microestrutural foi realizada por microscopia óptica e microscopia eletrônica de varredura. As observações experimentais mostraram uma diminuição da tenacidade ao impacto no material tratado termicamente, com uma tendência para uma queda maior com o aumento da temperatura do tratamento térmico. Este comportamento pode ser atribuído principalmente à precipitação e crescimento de carbonetos. Não foi observada a presença de mecanismos de fratura intergranular. Provavelmente o metal de solda estudado não possuía nível de impurezas suficiente para a ativação deste mecanismo.
Título em inglês
Influence of Postweld Heat Treatment in Microstructure and Mechanical Behavior of Weld Obtained by Rutile Flux-Cored Wire
Palavras-chave em inglês
Impact toughness
Microstructure
Rutile flux-cored wire
Stress relief
Resumo em inglês
The objective of this Dissertation was to analyze the effect of postweld heat treatment on microstructure and mechanical behavior of welds obtained by flux cored wire AWS E-81T1 Ni1. It was welded a joint with 60 mm thickness, on vertical position and ascendant progress. This joint was divided in three parts, one maintained as welded and two others heat treated for 6 hours on different temperatures, 585 °C and 650 °C. The effect of the heat treatment on mechanical properties was evaluated by means of hardness, tensile and impact Charpy-V tests. The characterization of the microstructure was undertaken utilizing optical and scanning electron microscopy. The experimental results revealed a decrease of impact toughness in heat treated material, with a tendency to a low impact toughness for high heat treatment temperature. This behavior may principally be attributed to an increase precipitation and growth of carbides. No intergranular fracture mechanism was observed. Probably the level of impurities in the weld metal studied was not high enough to provoke such phenomena.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD08006.pdf (14.13 Mbytes)
Data de Publicação
2013-08-20
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.