Mémoire de Maîtrise
DOI
10.11606/D.97.2011.tde-22082013-165145
Document
Auteur
Nom complet
Filipe Corrêa Pinto
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
Lorena, 2011
Directeur
Jury
Sandim, Hugo Ricardo Zschommler (Président)
Baptista, Carlos Antonio Reis Pereira
Pinto, Haroldo Cavalcanti
Titre en portugais
Caracterização mecânica e microestrutural do aço API 5L - X65 soldado por feixe de elétrons
Mots-clés en portugais
Aços API 5L-X65
Aços ARBL
Constituintes Microestruturais
Soldagem por feixe de elétrons
Resumé en portugais
O objetivo deste trabalho é a caracterização mecânica e microestrutural do aço API 5L-X65 soldado por feixe de elétrons para possível aplicação no processo de fabricação de dutos para o transporte de óleo e gás. A caracterização do material será realizada por meio de microscopia ótica, análise de textura via difração de raios X, microdureza Vickers e ensaio Charpy V. Para a caracterização microestrutural, foram testados diferentes ataques químicos para a identificação das fases presentes na microestrutura de cada uma das três regiões que compõem uma junta soldada, zona fundida (ZF), zona termicamente afetada (ZTA) e o metal base (MB). As microestruturas das regiões que foram submetidas ao ciclo térmico de soldagem, apresentaram-se bastante distintas da microestrutura bandeada ferrítico-perlítica encontrada no MB. A ZTA apresentou uma estrutura de grãos refinados, as bandas perlíticas do MB se tornaram completamente difusas, não mantendo qualquer semelhança com a microestrutura perlítica anterior e também, foram evidenciadas ilhas do constituinte M-A (martensita-austenita). Na ZF foram evidenciadas as fases tipicamente encontradas em metais de solda de aços microligados, tais como: ferrita de Widmanstätten, acicular, alotriomórfica, além de bainita e ilhas do constituinte M-A. Os resultados das propriedades mecânicas do material submetido ao processo de soldagem por EBW foram satisfatórios e atendem os requisitos da Norma API 5L. Desta forma, de acordo com os resultados obtidos neste trabalho é possível a aplicação da soldagem por EBW na fabricação e montagem de sistemas de dutos.
Titre en anglais
Mechanical and microstructural characterization of API 5L - X65 steel welded by electron beam
Mots-clés en anglais
API 5L-X65 steels
Electron beam welding
HSLA steels
Microstructural constituints
Resumé en anglais
The aim of this work is the mechanical and microstructural characterization of API 5L-X65 steel welds performed by electron beam welding, as well as to investigate the technical feasibility of applying this welding process in the manufacture and assembly of pipelines for oil and gas. The characterization was carried out by using light optical microscopy, X-ray diffraction texture analysis, Vickers micro-hardness testing and tests Charpy V. For the microstructural characterization, several chemical etchants were tested in order to identify the phases present in the microstructure of the regions associated to the weld, i.e. the weld metal (WM), the heat affected zone (HAZ) and the base metal (BM). The microstructures of the regions exposed to thermal welding cycles displayed quite distinct microstructure than the one found in the BM (banded ferritic-pearlitic structure). The HAZ showed a refined grain structure where the pearlite bands of BM became quite diffuse. Islands of the M-A (martensite-austenite) constituent were found in the HAZ. The phases typically found in weld metals of microalloyed steels such as Widmanstätten ferrite, acicular ferrite, allotriomorphic ferrite, bainite, and M-A constituent were found in the WM. The results of the mechanical properties of the material submitted to the welding process by EBW were satisfactory and meet the requirements of the standard API 5L. Thus, the according to the results obtained in this work is possible the application of EBW in the manufacture and assembly of pipeline systems.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
EMD11006.pdf (7.11 Mbytes)
Date de Publication
2013-08-22
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.