Dissertação de Mestrado
DOI
10.11606/D.97.2011.tde-23082013-105827
Documento
Autor
Nome completo
Paulo Roberto Godoy Patrocinio
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
Lorena, 2011
Orientador
Banca examinadora
Sandim, Hugo Ricardo Zschommler (Presidente)
Coelho, Gilberto Carvalho
Lins, Jefferson Fabrício Cardoso
Título em português
Caracterização da textura e do orelhamento ("earing"") da liga AA3104 após a redução a frio
Palavras-chave em português
Alumínio
Laminação
Latas de bebidas
Liga AA3104
Textura
Resumo em português
A liga de alumínio AA3104 é utilizada na manufatura de componentes obtidos via estampagem profunda e estiramento, como corpo de latas de bebidas. O presente trabalho visa relatar as principais alterações microestruturais e texturais da liga AA3104 em diferentes condições de deformação a frio. As amostras investigadas foram obtidas por meio de laminação a quente nas espessuras de 1,80 e 2,25 mm. O material A com espessura de 1,80 mm foi laminado duas vezes a frio com reduções de 64% e 59%. Já o material B com espessura de 2,25 mm foi laminado três vezes a frio com reduções de 55%, 52% e 51%. Após cada redução a frio foram retiradas amostras para as caracterizações. A espessura final nos dois materiais foi de 260 ?m. A caracterização microestrutural foi realizada por meio de microscopia ótica convencional e microscopia eletrônica de varredura. A textura de recristalização foi obtida por meio de difração de raios X. Foram realizados ensaios mecânicos para determinar a microdureza e limites de resistência e escoamento das amostras analisadas, além do ensaio de embutimento das amostras para a caracterização do orelhamento. Os melhores resultados de orelhamento foram obtidos no material A e os maiores valores de tensão de escoamento, resistência a tração e microdureza foram observadas no material B. Também foram retiradas amostras de latas de bebidas após a estampagem e após a estampagem e recozimento para a caracterização microestrutural. A ênfase desta Dissertação visa avaliar a influência da quantidade de deformação a frio aplicada em chapas recristalizadas provenientes da laminação a quente na textura cristalográfica e no comportamento das chapas durante o ensaio de orelhamento.
Título em inglês
Texture and earing characterization of AA3104 alloy after cold rolling
Palavras-chave em inglês
Alloy AA3104
Aluminum
Beverage can
Rolling
Texture
Resumo em inglês
The aluminum alloy AA3104 is widely used in the manufacture of components obtained by deep drawing and ironing, as the body of beverage cans. The present work describes the main microstructural and textural changes of AA3104 alloy following different cold rolling schedules. The samples were obtained after hot rolling, with thicknesses of 1.80 and 2.25 mm. Material A (1.80 mm) was cold rolled in two steps with reductions of 64% and 59%, respectively. Material B (2.25 mm) was cold rolled in three steps with reductions of 55%, 52% and 51% respectively. After each cold reduction samples were removed for microstructural characterization. The final thickness of the two materials was 260 ?m. The microstructural characterization was performed using conventional light optical and scanning electron microscopy. The recrystallization texture was determined by X-ray diffraction measurements. Mechanical tests were carried out to determine the Vickers microhardness as well as yield and tensile strengths. Deep drawing tests were performed for earing characterization. The best results of earing were obtained in material B. The highest yield and tensile strengths were observed in material A. Samples of commercial beverage cans were taken after deep drawing and annealing (drying) for microstructural characterization. The emphasis of this study is to evaluate the influence of the cold deformation in hot-rolled sheets regarding crystallographic texture evolution and corresponding behavior during earing tests.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
EMD11011.pdf (4.59 Mbytes)
Data de Publicação
2013-08-23
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.