Disertación de Maestría
DOI
10.11606/D.97.2016.tde-24072014-154227
Documento
Autor
Nombre completo
Maria Gabriela Galvão Camarinha
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2014
Director
Tribunal
Baptista, Carlos Antonio Reis Pereira (Presidente)
Barboza, Miguel Justino Ribeiro
Torres, Marcelo Augusto Santos
Título en portugués
Avaliação do comportamento em fadiga do aço maraging 300 submetido a processo de soldagem a laser
Palabras clave en portugués
Aço Maraging
Fadiga
Soldagem a Laser
Resumen en portugués
Os aços maraging pertencem a uma classe de aços de ultra-alta-resistência que diferem da maioria dos aços pelo mecanismo de endurecimento. Enquanto nos aços convencionais o endurecimento é obtido por transformação martensítica, nos aços maraging o aumento das propriedades mecânicas é obtido pela precipitação de compostos intermetálicos em uma matriz martensítica de baixo teor de carbono, em temperaturas da ordem de 480°C. Para o presente trabalho, empregou-se um aço maraging 300 na forma de barras cilíndricas com diâmetro de 8mm e comprimento de 120mm, cedido na condição solubilizada pelo Departamento de Ciência e Tecnologia Aeroespacial (DCTA). Os corpos-de-prova foram soldados em cheio empregando-se um laser a fibra de 2kW e um dispositivo especialmente desenvolvido para solda orbital. As condições de envelhecimento foram inicialmente estudadas e a melhor combinação de resistência mecânica e ductilidade foi obtidas na condição de para 460°C por 3 horas, que foi então adotada para a caracterização do comportamento em fadiga. Os ensaios de fadiga foram realizados em uma máquina de flexão rotativa (R = -1), em níveis de tensão correspondentes à faixa de vida de 104 a 107 ciclos. Os corpos-de-prova soldados a laser foram submetidos a três condições de tratamento pós-soldagem: a) envelhecimento, b) solubilização + envelhecimento e c) homogeneização + solubilização + envelhecimento. Os resultados permitiram avaliar e comparar o efeito da solda a laser, seguida por tratamentos térmicos pós-soldagem, no comportamento em fadiga do aço maraging 300. Os tratamentos pós-soldagem não resultaram em diferença significativa na vida em fadiga do aço maraging 300, o fator determinante para a duração da vida em fadiga foi a quantidade de poros presente na superfície de fratura.
Título en inglés
Evaluation of the fatigue behavior of maraging 300 steel subjected to laser welding process
Palabras clave en inglés
Fatigue
Laser Beam Weld
Maraging Steel
Resumen en inglés
The maraging steels belong to a class of ultra-high-resistance steels that differ from most of steel for the hardening mechanism. While the conventional steel is obtained by hardening for martensitic transformation in maraging steel the increase of mechanical properties is obtained by the precipitation of intermetallic phases in a martensitic matrix of low carbon, at temperatures about 480°C. For the present study, we used a maraging 300 steel in form of cylindrical bars with a diameter of 8mm and length of 120mm, received as solution treated by the Department of Aerospace Science and Technology (DCTA). The test specimens were welded using a 2 kW fibre laser coupled to a special lathe in order to obtain an orbital weld line. The ageing contitions of the steel were initially investigated using base material samples. The best combination of hardness, tensile strength and ductility were achieved for 460°C for 3 hours , which was then chosen for the fatigue characterization..The fatigue tests were conducted in a rotating bending machine (R = -1). The stress levels were found for fatigue lives in the range of 104 to 107 cycles. The laser welded test pieces underwent three distinct post-weld heat treatments: a) ageing , b) solution + ageing and b) homogenization + solution + ageing .The results allowed assessing and comparing the effect of laser beam welding, followed by post-weld heat treatments, on the fatigue behavior of the maraging 300 steel. The post-weld heat treatments no results in significant difference in fatigue life of maraging 300 steel , the determinant factor for fatigue life was the amount of pores present in the fracture surface.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD13006_O.pdf (6.18 Mbytes)
Fecha de Publicación
2016-09-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.