Disertación de Maestría
DOI
10.11606/D.97.2011.tde-26082013-101102
Documento
Autor
Nombre completo
Bruno Galvão Simba
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2011
Director
Tribunal
Santos, Claudinei dos (Presidente)
Strecker, Kurt
Suzuki, Paulo Atsushi
Título en portugués
Recuperação da fase tetragonal em cerâmicas dentárias à base de ZrO2(Y2O3) submetidas à transformação martensítica precoce
Palabras clave en portugués
Cerâmica dentária
Recuperação de fase
Zircônia
Resumen en portugués
Cerâmicas à base de zircônia tetragonal estabilizada com ítria (ZrO2(3%Y2O3)) possuem excelentes propriedades mecânicas, devido a uma peculiar transformação de fases que ocorre nos grãos desta cerâmica durante o crescimento de uma trinca. O crescimento da trinca gera tensões compressivas sobre os grãos tetragonais metaestáveis, os quais se transformam em monoclínicos, promovendo uma expansão volumétrica de 3 a 5%, a qual impede que a trinca continue crescendo nas condições de carregamento mecânicos inicialmente utilizados, o que produz aumento da resistência à fratura, e tenacidade deste material. Neste trabalho são apresentados os resultados do estudo da recuperação da fase tetragonal pela utilização de tratamentos térmicos, em zircônia envelhecida por desgaste, durante a preparação de próteses dentárias. Blocos cerâmicos pré-sinterizados à base de ZrO2(3%Y2O3) foram sinterizados em três condições distintas, quais sejam, 1450°C - 0h, 1530°C - 2h e 1600°C - 4h. Cada lote de amostras sinterizado foi submetido análise de densidade relativa, difração de raios X (DRX) e microscopia eletrônica de varredura (MEV). Parte das cerâmicas sinterizada foi fraturada, e a superfície de fratura foi re-examinada por DRX e MEV. Outra parte foi fragmentada visando a transformação martensítica, que gera a fase monoclínica no material, e em seguida caracterizada por DRX. Os resultados da densificação e análise microestrutural indicaram densidade relativa de 94,2%, 99,6% e 99,75%, tamanho médio de grão de 0,28?m, 0,49m e 1,31m, para amostras sinterizadas a 1450°C - 0h, 1530°C - 2h e 1600°C - 4h respectivamente. Após fragmentação, os teores de fase monoclínica medidos foram da ordem de 58%, 43% e 4,5% que correspondem a aproximadamente 65% vol, 50% vol e 6% vol. Tratamentos térmicos realizados a 950°C, 1100°C e 1200°C foram necessárias para recuperação de 100% de fase tetragonal, em amostras sinterizadas a 1450°C - 0h, 1530°C - 2h e 1600°C - 4h, respectivamente.
Título en inglés
Recovery of tetragonal phase in ZrO2 (Y2O3) dental ceramic submitted to forced martensitic transformation
Palabras clave en inglés
Dental ceramic
Phase recovery
Zirconia
Resumen en inglés
Tetragonal zirconia-based ceramic stabilized with (ZrO2(3%Y2O3)) have excellent mechanical properties due to a peculiar phase transformation that occurs in this ceramic grains during the growth of a crack. The crack growth generates compressive stresses on the metastable tetragonal grains, which are transformed into monoclinic, promoting a volumetric expansion of 3 to 5% which prevents the crack continues to grow under conditions of mechanical loading initially used, which produces the increased fracture strength and toughness of this material. This paper presents results of the recovery of the tetragonal phase by the use of thermal treatments in zirconia aged for wear during the preparation of dental prostheses. ZrO2(3%Y2O3) pre-sintered ceramic blocks were sintered in three different conditions: 1450°C-0h, 1530°C-2h and 1600°C-4h. Sintered samples were characterized by relative density, X-Ray diffraction (XRD) and Scanning Electron Microscopy (SEM). Part of the sintered samples was fractured and the fracture surface was re-examined by XRD and SEM. Another part was milled aiming generates a martensitic transformation (monoclinic phase), and characterized by XRD. The results of densification and SEM analysis indicates relative density of 94.2%, 99.6% and 99.75%, average grain size of 0.28?m, 0.48m and 1.31m, for samples sintered at 1450°C-0h, 1530°C-2h and 1600°C-4h respectively. After milling, the monoclinic phase content was 58%, 43% e 4,5% corresponding to 65% vol, 50% vol e 6% vol. For samples sintered at 1450°C-0h, 1530°C-2h e 1600°C-4h, heat treatments of 950°C, 1100°C and 1200°C were performed respectively, for recuperation of 100% of tetragonal phase.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD11013.pdf (2.58 Mbytes)
Fecha de Publicación
2013-08-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.