Disertación de Maestría
DOI
10.11606/D.97.2009.tde-27092012-120450
Documento
Autor
Nombre completo
Gabriel Godinho Alves
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2009
Director
Tribunal
Sandim, Hugo Ricardo Zschommler (Presidente)
Barboza, Miguel Justino Ribeiro
Silva, André Luiz Vasconcellos da Costa e
Título en portugués
Recristalização do aço ARBL microligado ao nióbio CSN 2336
Palabras clave en portugués
Aços alta resistência baixa liga
Microligado ao nióbio
Modelo JMAK
Recristalização
Textura
Resumen en portugués
No presente trabalho estudou-se a recristalização do aço de alta resistência baixa liga (ARBL) microligado ao nióbio (160 ppm em peso) da Companhia Siderúrgica Nacional 2336 utilizado na fabricação de reforços estruturais para a indústria automobilística. A grande utilização deste tipo de aço pelas indústrias tem motivado o desenvolvimento de novas ligas capazes de atender a requisitos críticos de estampagem combinado com alta resistência mecânica. Amostras deste aço no estado laminado a quente foram deformadas posteriormente a frio em escala piloto com reduções de 50 e 70%, reduções típicas na indústria, e recozidas em banho de sal em temperaturas variando entre 600 e 700ºC em diferentes tempos. A evolução microestrutural das amostras no estado encruado e na condição recozida foi acompanhada utilizando-se as técnicas de microscopia ótica e eletrônica de varredura. As texturas de deformação e de recristalização foram determinadas via difração de raios X. A fração volumétrica recristalizada (Xv) e o tamanho de grão foram determinados com o auxílio de metalografia quantitativa nas amostras recozidas. Medidas de microdureza Vickers foram utilizadas para construir as curvas de encruamento e da cinética de amolecimento em função da temperatura de recozimento e comparadas com curvas construídas pelo primeiro método. Os resultados mostram que a recristalização ocorre em temperaturas acima de 650°C. Com auxílio de um gráfico de Xv contra A (fração amolecida), podemos observar a ocorrência de um desvio da idealidade a 650°C e 700°C. A explicação mais provável é a ocorrência de precipitação, especialmente para o aço menos deformado. Os valores do expoente de Avrami obtidos a partir das duas abordagens (medidas de microdureza e metalografia quantitativa) são apresentados e discutidos.
Título en inglés
Recrystallization of a Nb-added High Strength Low Alloy CSN 2336 steel
Palabras clave en inglés
High strength low alloy steels
JMAK Model
Recrystallization
Steel containing niobium
Texture
Resumen en inglés
The recrystallization of a high strength low alloy steel (HSLA) containing niobium (160 wt-ppm) was investigated. The HSLA steel, named CSN 2336, is used in the manufacture of structural parts for automotive industry. The increasing use of this application type of steels in automotive industries has motivated the development of new alloys able to gather the critical requirements for deep drawing combined with high strengths. Samples of this steel in hot-rolled condition were cold-rolled with reductions of 50% and 70%, commonly used in most of applications, and isothermally annealed in salt bath at temperatures between 600 and 700ºC. The microstructure of the samples in both coldworked and annealed states was imaged using light optical (LOM) and scanning electronic microscopies (SEM). Deformation and recrystallization textures were determined by X-ray diffraction. The recrystallized volume fraction (Xv) and the mean grain size were determined by quantitative metallography in the annealed samples. Vickers microhardness testing was used to determine the work hardening and the softening kinetics behaviors. The results show that recrystallization occurs at temperatures above 650°C for the most deformed steel. By plotting Xv against A (softening fraction), we observe the occurrence of a deviation from ideality at 650°C and 700°C, likely caused by solid-state precipitation, especially for the less deformed steel. The values of n (Avrami exponent) obtained from both approaches (softening curves and quantitative metallography) are presented and discussed.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD09005.pdf (10.47 Mbytes)
Fecha de Publicación
2012-09-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.