Disertación de Maestría
DOI
10.11606/D.97.2010.tde-20082013-143254
Documento
Autor
Nombre completo
Leandro Marcos Salgado Alves
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2010
Director
Tribunal
Santos, Carlos Alberto Moreira dos (Presidente)
Nunes, Cristina Bórmio
Silva, Robson Ricardo da
Título en portugués
Comportamento elétrico não convencional no KxMoO2-δ
Palabras clave en portugués
Condutores unidimensionais.
KxMoO2-δ
Resistividade anômala
Resumen en portugués
Molibdatos têm atraído grande atenção devido à existência de compostos com caráter elétrico unidimensional como conseqüência da presença de cadeias contendo ligações de Mo-O ou Mo-Mo em suas estruturas cristalinas. Com o objetivo de estudar molibdatos com esta característica, amostras policristalinas do sistema K-Mo-O foram preparadas pelo método de reação de difusão no estado sólido e caracterizadas por difratometria de raios x, propriedades elétricas e magnéticas. Estes resultados demonstram a existência de uma nova fase neste sistema com estequiometria KxMoO2-δ. Medidas da resistência elétrica em função da temperatura deste material mostram comportamento metálico anômalo que está relacionado a um ordenamento antiferromagnético. Foi observado ainda que a anomalia na resistência elétrica em baixas temperaturas (T < TM) comporta-se segundo uma lei de potência com expoente próximo de 0,5, o que sugere que o comportamento elétrico do KxMoO2-δ pode ser descrito por um mecanismo de condutividade unidimensional.
Título en inglés
Unconvetional Electrical Behavior in the KxMoO2-δ
Palabras clave en inglés
Anomalous resistivity
KxMoO2-δ
One-dimensional conductors
Resumen en inglés
Molybdates have attracted great attention due to the existence of compounds which show one-dimensional electrical behavior as consequence of the channel containing Mo-O or Mo-Mo bonds in their crystalline structure. In order to study molybdates exhibiting onedimensional conductivity, polycrystalline samples of the K-Mo-O system were prepared using the solid state diffusion reaction method and characterized by X-ray powder diffractometry, electrical and magnetic properties. These results demonstrate the existence of a new phase in this system with KxMoO2-δ stoichiometry. Electrical resistance as a function of temperature measurements for this compound have shown anomalous metallic behavior which is related to an antiferromagnetic ordering. It has been also observed that the anomaly in the electrical resistance at low temperatures (T < TM) is fitted by power law temperature dependence with an exponent near 0.5 which suggests that the electrical behavior of the KxMoO2-δ can be well described by the one-dimensional conducting mechanism.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD10002.pdf (1.01 Mbytes)
Fecha de Publicación
2013-08-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.