Disertación de Maestría
DOI
10.11606/D.97.2008.tde-20082013-155902
Documento
Autor
Nombre completo
Lucas Barboza Sarno da Silva
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2008
Director
Tribunal
Rodrigues Junior, Durval (Presidente)
Lisboa Filho, Paulo Noronha
Suzuki, Paulo Atsushi
Título en portugués
Influência dos perfis de tratamentos térmicos nos processos de difusão, reação e formação de fases em supercondutores nanoestrusturados de Nb3Sn
Palabras clave en portugués
Aprisionamento de fluxo
Centros de aprisionamento artificiais
Dimensões nanométricas
Nb3Sn
Tratamento térmico
Resumen en portugués
Em trabalhos anteriores de nosso grupo de pesquisa foram desenvolvidos fios supercondutores nanoestruturados de Nb3Sn com introdução de centros de aprisionamento artificiais (CAAs) de Cu(Sn), numa tentativa de melhorar as propriedades supercondutoras. Porém, os perfis de tratamentos térmicos utilizados não foram otimizados. No presente trabalho as amostras desses fios compósitos foram utilizadas para otimização dos perfis de tratamentos térmicos visando determinar a influência destes perfis no processo de difusão atômica, reação e formação de fases nestes supercondutores nanoestruturados, e, com isso, otimizar a capacidade de transporte de corrente desses materiais. As micrografias e as análises composicionais obtidas produziram um conjunto de informações sobre os mecanismos de difusão e formação da fase supercondutora de Nb3Sn. As amostras foram analisadas quanto às suas propriedades e características supercondutoras. Com as medidas de transporte e magnetização pôde-se obter o comportamento global do supercondutor e o comportamento de cada filamento individual de Nb3Sn, respectivamente. Os compósitos otimizados apresentaram valores de temperatura crítica Tc próximos de 17 K, valores de Bc2 da ordem de 18 T, e densidades de corrente crítica tão altas quanto 1750 A/mm² a 4,2K e 12 T. Os máximos das curvas de força de aprisionamento aconteceram em campos magnéticos tão altos quanto 10 T, aproximadamente 0,5 Bc2, em distinção ao valor de 4,5 T (cerca de 0,2 Bc2) para Nb3Sn convencional, deslocamento que demonstra mudanças no comportamento de aprisionamento de fluxo nestes materiais. Um comportamento inédito e importante, que mistura os mecanismos de aprisionamento de fluxo devido aos contornos de grãos e as fases normais, está presente e pôde ser quantificado em detalhe. A análise dos comportamentos de todas as amostras possibilitou um entendimento satisfatório da influência dos CAAs na fase supercondutora e da influência do efeito de proximidade no aprisionamento de fluxo e nas propriedades de transporte destes materiais.
Título en inglés
Influence of the heat treatment profiles on the processes of diffusion, reaction and formation of phases in nanostructured Nb3Sn superconductors
Palabras clave en inglés
Artificial pinning centers
Flux pinning
Heat treatment
Nanometric dimensions
Nb3Sn
Resumen en inglés
In previous works of our research group it was shown the development of Nb3Sn nanostructured superconducting wires with introduction of artificial pinning centers (APCs) of Cu(Sn), in an attempt to improve the superconducting properties. However, the used heat treatment profiles were not optimized. In the present work samples of these composite wires were used to optimize the heat treatment profile aiming to determine the influence of these profiles on the processes of atomic diffusion, reaction and formation of phases in these nanostructured superconductors and, consequently, optimize the transport properties of these materials. The obtained micrographs and compositional analysis gave a set of information about the diffusion mechanisms and formation of the Nb3Sn superconducting phase. The samples were analyzed in relation to their superconducting properties and characteristics. The transport and magnetization measurements showed the global behavior of the superconductor and the behavior of each individual Nb3Sn filament, respectively. The optimized composites presented values of critical temperature Tc around 17 K, values of Bc2 around 18 T, and critical current densities as large as 1750 A/mm2 at 4,2 K and 12 T. The peaks of the pinning force curves, occurred at magnetic fields as large as 10 T, approximately 0.5 Bc2, in distinction to the value of 4.5 T (about 0.2 Bc2) for conventional Nb3Sn, displacement that demonstrates changes on the flux pinning behavior in these materials. An inedit and important behavior, which mixes the flux pinning mechanisms due to the grain boundaries and to the normal phases, is present and could be quantified in detail. The behavior analysis of all samples enable a satisfactory understanding of the APCs influence on the superconducting phase and of the influence of the proximity effect on the flux pinning and on the transport properties of these materials.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMD08007.pdf (6.57 Mbytes)
Fecha de Publicación
2013-08-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.