Tesis Doctoral
DOI
10.11606/T.97.2008.tde-20082013-163321
Documento
Autor
Nombre completo
Mário Sérgio da Luz
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2008
Director
Tribunal
Santos, Carlos Alberto Moreira dos (Presidente)
Granato, Enzo
Kopelevitch, Iakov Veniaminovitch
Nunes, Cristina Bórmio
Shigue, Carlos Yujiro
Título en portugués
Efeito Hall em supercondutores a campo magnético nulo
Palabras clave en portugués
Efeito Hall
Granularidade
Materiais anisotropicos
Supercondutividade
Resumen en portugués
Este trabalho reporta a influencia da granularidade sobre a resistencia transversal em funcao da temperatura, RXY(T), medidas em amostras policristalinas dos sistemas supercondutores Bi2Sr2Ca-1-xPrxCu2O8+??e YBa2Cu3O7-?, e em monocristais de composicao Li0,9Mo6O17. Foi observada tensao nao nula na voltagem Hall, em campo magnetico aplicado nulo, nas proximidades da temperatura de transicao supercondutora (TC), para os tres sistemas em questao. A tensao Hall a campo zero se manifesta atraves de picos abaixo de TC, que esta relacionada com a componente longitudinal da resistencia e, por consequencia, com o carater granular das amostras. E apresentada tambem a existencia de uma assimetria no sinal Hall em campo magnetico aplicado. Estes comportamentos sao discutidos baseado no movimento de vortices e anti-vortices, de Josephson e Abrikosov no interior das amostras. Para monocristais de Li0,9Mo6O17 tambem foi observado efeito Hall a campo magnetico nulo. Alem do mais, uma nova relacao de anisotropia confirma o carater qause-unidmensional deste composto, mas mostra uma anisotropia menor do que aquela reportada previamente. Foi observado tambem que este material apresenta transicoes do tipo supercondutor-isolante (SIT) e metal- isolante (MIT) em temperaturas proximas ao zero absoluto.
Título en inglés
Hall Effect in Superconductors at Zero Magnetic Field
Palabras clave en inglés
Anisotropic Materials
Granularity
Hall Effect
Superconductivity
Resumen en inglés
This work reports the influence of the granularity on the transverse resistance as a function of temperature, RXY(T), in Bi2Sr2Ca1-xPrxCu2O8+??and YBa2Cu3O7-??polycrystalline samples, and Li0.9Mo6O17 single crystals. The effects of warming rate, temperature, applied magnetic field, and electrical current on the Hall resistance are reported. At zero magnetic field two peaks are observed in RXY(T) curves for the three compounds. The peaks are related to the double superconducting transition in the longitudinal component RXX(T) curves. In the superconducting and normal states no transverse voltage has been detected at zero magnetic field, as expected. The results are discussed within the framework of the motion of Abrikosov and Josephson vortices and anti-vortices. A new scaling relation between transverse and longitudinal voltages given by RXY ~ dRXX/dT has been confirmed. Regarding Li0.9Mo6O17 single crystals, Hall resistance at zero applied magnetic field was also observed. Furthermore, the results confirm the quasi-unidimensionality but show smaller anisotropic ratio than previously reported. Simultaneously, the result reveals that the Li0.9Mo6O17 is the first bulk superconducting compound exhibiting superconductor-insulator-transition (SIT) and metal-insulator-transition (MIT) behaviors.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT08004.pdf (3.35 Mbytes)
Fecha de Publicación
2013-08-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.