Tesis Doctoral
DOI
10.11606/T.97.2010.tde-26092012-172415
Documento
Autor
Nombre completo
Eliana Cursino
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2010
Director
Tribunal
Rodrigues Junior, Durval (Presidente)
Santos, Claudinei dos
Carvalho, Claudio Luiz
Neves, Marcelo Azevedo
Ribeiro, Sebastiao
Título en portugués
Obtenção e caracterização de supercondutores de Bi2212 texturizados com introdução de centros artificiais de aprisionamento
Palabras clave en portugués
Centros artificiais de aprisionamento
Difratometria de raios X
Microscopia eletrônica de transmissão
Microscopia eletrônica de varredura
Supercondutividade
Resumen en portugués
O presente trabalho analisou as condições de texturização de amostras de Ag/Bi2212 (Bi2Sr2CaCu2O8+δ) na forma de pastilhas e de fitas, verificando-se a influência do tratamento térmico, atmosfera, adição de prata e adição de zircônia ou zirconato de cálcio. As adições de zircônia ou de zirconato de cálcio, com partículas de dimensões submicrométricas ou nanométricas (abaixo de 200nm), foram analisadas como possíveis geradores de centros de aprisionamento de fluxo magnético, assim como foi feita a análise de seus comportamentos nas propriedades intrínsecas da matriz supercondutora. A influência da atmosfera de tratamento térmico foi analisada de modo a alterar a concentração de oxigênio na fase supercondutora visando melhores resultados de temperatura crítica, sem depreciação das densidades de corrente crítica e dos campos de irreversibilidade, Birr. Foram analisadas as influências dos parâmetros de tratamento térmico, tais como temperatura máxima de reação, tempo nesta temperatura máxima, taxa de resfriamento do estado líquido ao estado sólido, e temperatura e tempo de recozimento após solidificação. Verificou-se a influência do resfriamento do forno sobre a texturização e a temperatura crítica. Quanto à dopagem com prata, foi verificada sua influência na texturização e interação com a zircônia. Foram realizadas caracterizações supercondutoras e microestruturais das amostras.
Título en inglés
Production and characterization of textured Bi2212 superconductors with introduction of artificial pinning centers.
Palabras clave en inglés
Artificial pinning centers
Scanning electron microscopy
Superconductivity
Transmission electron microscopy
X-ray diffractometry
Resumen en inglés
The present work analyzed the texturing conditions of Ag/Bi2212 samples (Bi2Sr2CaCu2O8+δ) in the form of bulks and of tapes, verifying the influence of heat treatment, atmosphere, silver addition and addition of zirconia or calcium zirconate. The additions of zirconia or calcium zirconate, with particles of submicron or nanometric (below 200nm) dimensions, were analyzed as possible generators of magnetic flux pinning centers, as well as it was analyzed their behaviors on the intrinsic properties of the superconducting matrix. The influence of the heat treatment atmosphere was analyzed in order to change the oxygen concentration in the superconducting phase aiming better results of critical temperature, without depreciation of the critical current densities and of the irreversibility fields, Birr. The influences of the heat treatment parameters were analyzed, such as the reaction maximum temperature, soaking time at this maximum temperature, cooling rate from the liquid to the solid states, and annealing temperature and time after solidification. It was verified the influence of the furnace cooling rate on the texturing and critical temperatures. Concerning to the silver addition, it was verified its influence on the texturing and its interaction with the zirconia. Superconducting and microstructural characterizations of the samples were performed.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT10003.pdf (9.09 Mbytes)
Fecha de Publicación
2012-09-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.