Tesis de Habilitación
DOI
10.11606/T.18.2011.tde-21032011-094057
Documento
Autor
Nombre completo
Marcelo Falcão de Oliveira
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2010
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Casteletti, Luiz Carlos
Goldenstein, Helio
Nunes, Carlos Angelo
Tenorio, Jorge Alberto Soares
Título en portugués
Um novo critério para a formulação de ligas metálicas vítreas.
Palabras clave en portugués
Ligas - formulação
Termodinâmica
Topologia
Vidros - formação
Vidros metálicos
Resumen en portugués
Essa tese apresenta um novo critério para a formulação de ligas metálicas com alta tendência à formação de vidros (TFV). O novo critério combina um parâmetro de mínima instabilidade topológica (lmin), usado como indicativo da competição de fases durante a solidificação, e um parâmetro termodinâmico (Dh) que depende da diferença média da função trabalho (Df) e da diferença média de densidade eletrônica (Dnws 1/3) entre os elementos que constituem as ligas. O parâmetro termodinâmico (Dh) apresentou um coeficiente de correlação de 0,75 em relação às taxas críticas de resfriamento (Rc) de 69 ligas, em 31 sistemas metálicos diferentes e reportadas pela literatura. A combinação desse parâmetro termodinâmico com a mínima instabilidade topológica (lmin) produziu um critério de previsão para a TFV com coeficiente de correlação de 0,71 em relação às taxas críticas de resfriamento (RC) dessas mesmas ligas. O critério gm, usado para avaliar a TFV, segundo temperaturas características de transformações das ligas (transição vítrea, Tg, cristalização, Tx, e final de fusão, Tl), apresentou um coeficiente de correlação de 0,84 indicando que o critério de previsão se ajusta razoavelmente bem ao que é experimentalmente observado. O novo critério foi ainda testado em dois sistemas conhecidos quanto à produção de vidros metálicos, Cu-Zr e Cu-Zr-Al. Para o sistema Cu-Zr observou-se um bom ajuste entre as máximas espessuras amorfas (Zc) previstas e aquelas experimentalmente observadas segundo a variação da concentração dos elementos metálicos na liga. Para o sistema Cu-Zr-Al a região de composições com maior TFV se aproxima muito da teoricamente prevista. A máxima Zc estimada (10 a 12 mm) é próxima da observada experimentalmente (10 mm) e a composição química dessa liga não está a mais de 10 at.% das composições que, teoricamente, deveriam apresentar maior TFV para o sistema Cu-Zr-Al.
Título en inglés
A new criterion for searching bulk metallic glass alloys.
Palabras clave en inglés
Alloy - composition
Glass formation
Metallic glass
Thermodynamics
Topology
Resumen en inglés
In this work a new criterion for selection of easy glass forming compositions in metallic alloys is introduced. The new criterion combines two distinct parameters: a topological parameter (lmin), which is an indicator of the local minimum topological instability for a crystalline phase, also related to the competition of phases during solidification; and a thermodynamic parameter (Dh), which is a function of the average difference of electron work functions (Df) and the average difference of electronic densities (Dnws 1/3) among the constitutive elements of the alloy. The thermodynamic parameter (Dh) presented a correlation coefficient of 0.75 regarding the critical cooling rates (Rc) of 69 alloys, in 31 metallic systems, reported by the literature. By combining this parameter (Dh) with the minimum topological instability (lmin) a correlation coefficient of 0.71 was found for the same reported critical cooling rates (RC). The gm criterion, useful to evaluate the glass forming ability (GFA) according to characteristc temperatures (glass transition, Tg, crystallization, Tx, and end of melting, Tl), presented a correlation coefficient of 0.84 indicating that the new prediction criterion is in good agreement with the experimental observations. The new criterion was further tested regarding two well known metallic systems in which many bulk metallic glasses (BMGs) have already been produced, Cu-Zr and Cu-Zr- Al. For the Cu-Zr alloys a nice fitting between the maximum amorphous thickness (Zc) curves, predicted and observed, was found as a function of the alloy chemical composition. For the Cu-Zr-Al system, the range of compositions predicted to show the highest GFA is close to the compositions of the reported BMGs. The maximum estimated amorphous thickness (Zc) (10-12 mm) compares with the maximum reported Zc (10 mm). Furthermore, the chemical composition of such BMG alloy is less than 10 at.% far from the chemical composition spot predicted to show the highest GFA in the Cu-Zr-Al system.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TeseLDfinal.pdf (611.13 Kbytes)
Fecha de Publicación
2011-03-21
 
ADVERTENCIA: El material descrito abajo se refiere a los trabajos derivados de esta tesis o disertación. El contenido de estos documentos es responsabilidad del autor de la tesis o disertación.
  • DE OLIVEIRA, Marcelo Falcão. A new correlation between electronic parameters and glass forming ability of metallic alloys [doi:10.1080/09500839.2011.579078]. Philosophical Magazine Letters [online], 2011, vol. 91, n. 6, p. 418-422.
  • DE OLIVEIRA, Marcelo Falcão. A simple criterion to predict the glass forming ability of metallic alloys [doi:10.1063/1.3676196]. Journal of Applied Physics [online], 2012, vol. 111, n. 2, p. 023509.