Tesis Doctoral
DOI
10.11606/T.58.2013.tde-06022014-083917
Documento
Autor
Nombre completo
Rodrigo Gonçalves Soares
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Ribeirão Preto, 2013
Director
Tribunal
Mazzetto, Marcelo Oliveira (Presidente)
Brandini, Daniela Atili
Carreiro, Adriana da Fonte Porto
Prado, Celio Jesus do
Reis, Andréa Candido dos
Título en portugués
Avaliação das propriedades mecânicas dos polipropilenos utilizados para confecção de placas oclusais
Palabras clave en portugués
placa oclusal
polipropileno
propriedades mecânicas
resina acrílica
Resumen en portugués
O objetivo desse estudo foi avaliar algumas propriedades mecânicas como a rugosidade de superfície, microdureza, módulo de elasticidade e resistência flexural dos polipropilenos em comparação com as resinas acrílicas. Para avaliação das propriedades foram confeccionados doze corpos de prova (65 x 10 x 3 mm) de cada marca comercial de resina acrílica: Vipi Flash (autopolimerizável), Vipi Wave (termopolimerizável por calor de microondas), Vipi Crill, Lucitone, QC-20 (termopolimerizáveis por calor de banho de água); e Bioflex (termoplástico do tipo rígido) e Flexsystem (termoplástico do tipo flexível). As médias e desvios padrões do teste de rugosidade superficial em Ra foram Vipi Flash (0,10 ± 0,03); Vipi Wave (0,10 ± 0,02); Vipi Cril (0,12 ± 0,04); Lucitone (0,10 ± 0,02); QC-20 (0,11 ± 0,03); Bioflex (0,13 ± 0,01) e Flexsystem (0,10 ± 0,02). Microdureza Knoop: Vipi Flash (15,36 ± 0,32); Vipi Wave (16,60 ± 0,87); Vipi Cril (18,89 ± 2,10); Lucitone (15,73 ± 0,33); QC-20 (15,91 ± 0,47); Bioflex (71,64 ± 3,99) e Flexsystem (65,37 ± 7,08). Módulo de elasticidade: Vipi Flash (2952,76 ± 292,12); Vipi Wave (2511,69 ± 304,09); Vipi Cril (2745,61± 288,86); Lucitone (1904,53 ± 149,05); QC-20 (1913,86 ± 147,80); Bioflex (523,57 ± 151,19) e Flexsystem (367,04 ± 171,61). Resistência flexural: Vipi Flash (81,62 ± 4,62); Vipi Wave (83,52 ± 8,42); Vipi Cril (64,17± 5,23); Lucitone (74,71± 9,03); QC-20 (75,80 ± 8,44); Bioflex (22,99 ± 5,46) e Flexsystem (22,99 ± 7,59). O polipropileno Bioflex apresentou o maior valor de rugosidade de superfície (p<0,05) e microdureza Knoop (p<0.01), quando comparado com as demais resinas avaliadas; e os polipropilenos Bioflex e Flexsystem apresentaram os menores valores do módulo de elasticidade (p<0.01) e resistência flexural (p<0.01), quando comparado com as demais resinas avaliadas.
Título en inglés
Evaluation of mechanical properties of the polypropylene used for the preparation of occlusal splints
Palabras clave en inglés
acrylic resin
mechanical properties
occlusal splint
polypropylene
Resumen en inglés
The aim of this study was to evaluate the mechanical properties such as surface roughness, hardness, elastic modulus and flexural strength of polypropylene compared to acrylic resins. To evaluate the properties were made twelve specimens (65 x 10 x 3 mm) of each brand acrylic resin: Vipi Flash (self-curing), Vipi Wave (thermo microwave heat), Vipi Crill, Lucitone QC - 20 (thermo heat water bath) and Bioflex (thermoplastic rigid type) and Flexsystem (thermoplastic flexible type). The means and standard deviations of the test surface roughness in Ra were Vipi Flash (0.10 ± 0.03); Vipi Wave (0.10 ± 0.02); Vipi Cril (0.12 ± 0.04); Lucitone (0.10 ± 0.02); QC -20 (0.11 ± 0.03) Bioflex (0.13 ± 0.01) and FlexSystem (0.10 ± 0.02). Knoop hardness: Vipi Flash (15.36 ± 0.32); Vipi Wave (16.60 ± 0.87); Vipi Cril (18.89 ± 2.10); Lucitone (15.73 ± 0.33); QC- 20 (15.91 ± 0.47); Bioflex (71.64 ± 3.99) and FlexSystem (65.37 ± 7.08). Modulus of elasticity: Vipi Flash (2952.76 ± 292.12); Vipi Wave (2511.69 ± 304.09); Vipi Cril (2745.61 ± 288.86); Lucitone (1904.53 ± 149.05), QC- 20 (1913.86 ± 147.80); Bioflex (523.57 ± 151.19) and FlexSystem (367.04 ± 171.61). Flexural strength: Vipi Flash (81.62 ± 4.62); Vipi Wave (83.52 ± 8.42); Vipi Cril (64.17 ± 5.23); Lucitone (74.71 ± 9.03); QC- 20 (75.80 ± 8.44) ; Bioflex (22.99 ± 5.46) and FlexSystem (22,99 ± 7,59). Polypropylene Bioflex showed the highest surface roughness (p < 0.05) and Knoop hardness (p < 0.01), when compared to other resins evaluated, and polypropylenes Bioflex and FlexSystem showed the lower modulus of elasticity (p < 0.01), and flexural strength (p < 0.01) as compared with other resins evaluated.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2014-10-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.